Kingfa JE2-R2G20 Glass Fiber Reinforced ABS/PBT Alloy

Category Polymer , Thermoplastic , ABS Polymer , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer Kingfa Sci. & Tech. Co.
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kingfa JE2-R2G20 Glass Fiber Reinforced ABS/PBT Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features:High stiffness, high hardnessGood mechanical strengthGood chemical resistanceGood size stabilityGood heat stabilityLow tendency to warpApplications:Optical appliance (camera, video)Sports appliancePrinter, photocopier cabinetScanner partsAutomobile instrument panelsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.36 g/cc

@Temperature 23.0 °C
1.36 g/cc

@Temperature 73.4 °F
ASTM D792
Linear Mold Shrinkage 0.0060 - 0.0090 cm/cm

@Temperature 23.0 °C
0.0060 - 0.0090 in/in

@Temperature 73.4 °F
Plumb; ASTM D955
Linear Mold Shrinkage, Flow 0.0030 - 0.0040 cm/cm

@Temperature 23.0 °C
0.0030 - 0.0040 in/in

@Temperature 73.4 °F
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell M 82
82
ASTM D785
Tensile Strength at Break 90.0 MPa
13100 psi
10mm/min; ASTM D638
Elongation at Break 5.0 %
5.0 %
10mm/min; ASTM D638
Flexural Strength 145 MPa
21000 psi
2mm/min; ASTM D790
Flexural Modulus 7.80 GPa
1130 ksi
2mm/min; ASTM D790
Izod Impact, Notched 0.750 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
1.41 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 122 °C

@Thickness 6.40 mm
252 °F

@Thickness 0.252 in
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 110 °C

@Thickness 6.40 mm
230 °F

@Thickness 0.252 in
ASTM D648
Flammability, UL94 V-2

@Thickness 1.60 mm
V-2

@Thickness 0.0630 in
V-2

@Thickness 3.30 mm
V-2

@Thickness 0.130 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Processing Properties Metric English Comments
Processing Temperature <= 265 °C
<= 509 °F
Rear Barrel Temperature 245 - 265 °C
473 - 509 °F
Start Point: 250°C
Middle Barrel Temperature 240 - 260 °C
464 - 500 °F
Start Point: 245°C
Front Barrel Temperature 235 - 260 °C
455 - 500 °F
Start Point: 240°C
Melt Temperature 235 - 260 °C
455 - 500 °F
Start Point: 250°C
Mold Temperature 60.0 - 110 °C
140 - 230 °F
Start Point: 90°C
Drying Temperature 100 - 110 °C

@Time 7200 - 10800 sec
212 - 230 °F

@Time 2.00 - 3.00 hour
Pre-dry
Back Pressure 0.300 - 1.00 MPa
43.5 - 145 psi
Descriptive Properties Value Comments
Injection Speed 60-80%