Kingfa JH710 G10 Flame Retardant & 10% Glass Reinforced PC

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass Fiber Filled, Flame Retardant
Manufacturer Kingfa Sci. & Tech. Co.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kingfa JH710 G10 Flame Retardant & 10% Glass Reinforced PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features:Environmental friendly flame retardantUL V-0 @ 1.6mmHigh mechanical strengthGood size stability, good surfaceSuitable for exact moldingApplications:CD-ROM, DVDPrinter, photocopier cabinetScanner partsExact mechanism partsElectrical appliance partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.26 g/cc

@Temperature 23.0 °C
1.26 g/cc

@Temperature 73.4 °F
ASTM D792
Linear Mold Shrinkage 0.0030 - 0.0040 cm/cm

@Temperature 23.0 °C
0.0030 - 0.0040 in/in

@Temperature 73.4 °F
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell M 84
84
ASTM D785
Tensile Strength at Break 75.0 MPa
10900 psi
10mm/min; ASTM D638
Elongation at Break 9.0 %
9.0 %
10mm/min; ASTM D638
Flexural Strength 105 MPa
15200 psi
2mm/min; ASTM D790
Flexural Modulus 4.20 GPa
609 ksi
2mm/min; ASTM D790
Izod Impact, Notched 1.08 J/cm

@Thickness 3.20 mm,
Temperature -30.0 °C
2.02 ft-lb/in

@Thickness 0.126 in,
Temperature -22.0 °F
ASTM D256
1.22 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
2.29 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 142 °C

@Thickness 6.40 mm
288 °F

@Thickness 0.252 in
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 130 °C

@Thickness 6.40 mm
266 °F

@Thickness 0.252 in
ASTM D648
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
ASTM D257
Dielectric Strength 19.0 kV/mm
483 kV/in
ASTM D149
Processing Properties Metric English Comments
Processing Temperature <= 280 °C
<= 536 °F
Rear Barrel Temperature 230 - 250 °C
446 - 482 °F
Start Point: 240°C
Middle Barrel Temperature 235 - 260 °C
455 - 500 °F
Start Point: 245°C
Front Barrel Temperature 240 - 270 °C
464 - 518 °F
Start Point: 250°C
Melt Temperature 235 - 260 °C
455 - 500 °F
Start Point: 240°C
Mold Temperature 80.0 - 110 °C
176 - 230 °F
Start Point: 90°C
Drying Temperature 110 - 120 °C

@Time 10800 - 14400 sec
230 - 248 °F

@Time 3.00 - 4.00 hour
Pre-dry
Back Pressure 0.300 - 1.00 MPa
43.5 - 145 psi
Descriptive Properties Value Comments
Glass Fiber Content (%) 10
Injection Speed 60-80%