Kingfa JH710 G10D Flame Retardant & 10% Glass Fiber Reinforced PC

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Glass Fiber Filled, Flame Retardant
Manufacturer Kingfa Sci. & Tech. Co.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kingfa JH710 G10D Flame Retardant & 10% Glass Fiber Reinforced PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features:Environmental friendly flame retardantUL V-0 @ 1.6mmHigh mechanical strengthGood size stability, good surfaceSuitable for exact moldingApplications:Exact mechanism partsElectrical and electronic partsPrinter, photocopier cabinetElectrical equipment partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.26 g/cc

@Temperature 23.0 °C
1.26 g/cc

@Temperature 73.4 °F
ASTM D792
Linear Mold Shrinkage 0.0030 - 0.0050 cm/cm

@Temperature 23.0 °C
0.0030 - 0.0050 in/in

@Temperature 73.4 °F
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell M 83
83
ASTM D785
Tensile Strength at Break 54.0 MPa
7830 psi
10mm/min; ASTM D638
Elongation at Break 18 %
18 %
10mm/min; ASTM D638
Flexural Strength 92.0 MPa
13300 psi
2mm/min; ASTM D790
Flexural Modulus 3.00 GPa
435 ksi
2mm/min; ASTM D790
Izod Impact, Notched 1.16 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
2.17 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Izod Impact, Unnotched 4.50 J/cm - NB

@Thickness 3.20 mm,
Temperature 23.0 °C
8.43 ft-lb/in - NB

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 130 °C

@Thickness 6.40 mm
266 °F

@Thickness 0.252 in
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 122 °C

@Thickness 6.40 mm
252 °F

@Thickness 0.252 in
ASTM D648
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
ASTM D257
Dielectric Strength 19.0 kV/mm
483 kV/in
ASTM D149
Processing Properties Metric English Comments
Processing Temperature <= 290 °C
<= 554 °F
Rear Barrel Temperature 235 - 260 °C
455 - 500 °F
Start Point: 245°C
Middle Barrel Temperature 240 - 270 °C
464 - 518 °F
Start Point: 250°C
Front Barrel Temperature 250 - 280 °C
482 - 536 °F
Start Point: 255°C
Melt Temperature 235 - 260 °C
455 - 500 °F
Start Point: 245°C
Mold Temperature 80.0 - 130 °C
176 - 266 °F
Start Point: 90°C
Drying Temperature 110 - 120 °C

@Time 14400 - 21600 sec
230 - 248 °F

@Time 4.00 - 6.00 hour
Pre-dry
Back Pressure 0.000 - 10.0 MPa
0.000 - 1450 psi
Descriptive Properties Value Comments
Glass Fiber Content (%) 10
Injection Speed 60-90%