Kingfa MAC-601 AC PC/ABS Alloy

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Kingfa Sci. & Tech. Co.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kingfa MAC-601 AC PC/ABS Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features:Excellent balance propertiesHigh impact strengthGood processing propertiesApplications:Injection moldingAutomobile instrument panelElectrical and electronic partsComputer and accessoriesHousehold appliance thin wall partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.13 g/cc

@Temperature 23.0 °C
1.13 g/cc

@Temperature 73.4 °F
ASTM D792
Water Absorption 0.30 %

@Temperature 23.0 °C,
Time 86400 sec
0.30 %

@Temperature 73.4 °F,
Time 24.0 hour
ASTM D570
Linear Mold Shrinkage 0.0030 - 0.0070 cm/cm

@Temperature 23.0 °C
0.0030 - 0.0070 in/in

@Temperature 73.4 °F
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118
118
ASTM D785
Tensile Strength at Break 50.0 MPa
7250 psi
50mm/min; ASTM D638
Elongation at Break 70 %
70 %
50mm/min; ASTM D638
Flexural Strength 80.0 MPa
11600 psi
2mm/min; ASTM D790
Flexural Modulus 2.30 GPa
334 ksi
2mm/min; ASTM D790
Izod Impact, Notched 5.00 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
9.37 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Izod Impact, Unnotched NB

@Thickness 3.20 mm,
Temperature 23.0 °C
NB

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 125 °C

@Thickness 6.40 mm
257 °F

@Thickness 0.252 in
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 105 °C

@Thickness 6.40 mm
221 °F

@Thickness 0.252 in
ASTM D648
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
ASTM D257
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
ASTM D257
Dielectric Strength >= 35.0 kV/mm
>= 889 kV/in
1.6mm; ASTM D149
Processing Properties Metric English Comments
Processing Temperature <= 280 °C
<= 536 °F
Rear Barrel Temperature 230 - 250 °C
446 - 482 °F
Start Point: 230°C
Middle Barrel Temperature 240 - 260 °C
464 - 500 °F
Start Point: 235°C
Front Barrel Temperature 250 - 280 °C
482 - 536 °F
Start Point: 240°C
Melt Temperature 240 - 280 °C
464 - 536 °F
Start Point: 245°C
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Start Point: 60°C
Drying Temperature 100 - 110 °C

@Time 14400 - 21600 sec
212 - 230 °F

@Time 4.00 - 6.00 hour
Pre-dry
Back Pressure 0.700 - 1.00 MPa
102 - 145 psi
Descriptive Properties Value Comments
Injection Speed 60-100%
Users viewing this material also viewed the following: