Kolon KOPEL® KP3372 General Purpose TPE Resin

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber
Manufacturer Kolon
Trade Name KOPEL®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kolon KOPEL® KP3372 General Purpose TPE Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
KOPEL® is a thermoplastic polyester elastomer which is a new engineering rubber having combined properties of conventional rubber and thermoplastic. Its flexibility and elastic recovery are very similar to rubber, but its processability is much superior to rubber. While its flexibility and elastic recovery are similar to rubber, its mechanical properties-heat resistance, weather resistance and UV stability-are far greater than the performance of rubber.Excellent flexibility and creep resistance, good mechanical properties and heat stability, good chemical resistanceInformation provided by US distributor, API-Kolon.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
DIN 53479; ASTM D792
Water Absorption 0.30 %
0.30 %
DIN 53475; ASTM D570
Linear Mold Shrinkage 0.016 - 0.019 cm/cm
0.016 - 0.019 in/in
ASTM D955
Melt Flow 17 g/10 min

@Temperature 230 °C
17 g/10 min

@Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 72
72
DIN 53505; ASTM D2240
Tensile Strength, Ultimate 39.2 MPa
5690 psi
DIN 53455; ASTM D638
Elongation at Break 400 %
400 %
DIN 53455; ASTM D638
Izod Impact, Notched 0.539 J/cm
1.01 ft-lb/in
Low Temp
2.55 J/cm
4.78 ft-lb/in
DIN 53453; ASTM D256
Taber Abrasion, mg/1000 Cycles 10
10
CS-17 WHEEL; ASTM D1044
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 148 °C
298 °F
DIN 53461; ASTM D648
Brittleness Temperature <= -65.0 °C
<= -85.0 °F
Solenoid Brittle Point; ASTM D746
Flammability, UL94 HB
HB