Kostat E-2001 Conductive PP Compound

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Kostat
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kostat E-2001 Conductive PP Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
KOSTAT E-2001 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using a special conductive carbon black. In addition to a low electrical resistivity, E-2001 has excellent mechanical properties and is easy to extrude. Typical applications include extrusion of corrugated sheets and sheers for electronics packaging. KOSTAT E-2001 is not dependant on atmospheric conditions.Special FeaturesThis product exhibits high conductivity, easy processing, smooth sheet surface, and tight dimensional tolerances after forming. This makes KOSTAT E-2001 ideal for thermoforming various packaging products.Applications:KOSTAT E-2001 is recommended for electronics packaging such as ESD sheets, formed tray sheets, and other extruded products.
Physical Properties Metric English Comments
Specific Gravity 1.09 g/cc
1.09 g/cc
ASTM D792
Melt Flow 0.50 g/10 min

@Load 5.00 kg,
Temperature 230 °C
0.50 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 75
75
ASTM D785
Tensile Strength, Yield 25.0 MPa
3630 psi
ASTM D638
Elongation at Break 20 %
20 %
ASTM D638
Flexural Strength 38.0 MPa
5510 psi
ASTM D790
Flexural Modulus 1.96 GPa
284 ksi
ASTM D790
Izod Impact, Notched 6.85 J/cm
12.8 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 105 °C
221 °F
ASTM D648
Electrical Properties Metric English Comments
Volume Resistivity 10000 ohm-cm
10000 ohm-cm
Kostat Rv
Surface Resistivity per Square 1e+05
1e+05
Kostat Rs
Processing Properties Metric English Comments
Rear Barrel Temperature 210 °C
410 °F
C1
Middle Barrel Temperature 220 °C
428 °F
C3
Front Barrel Temperature 230 °C
446 °F
C5
Die Temperature 104 °C
220 °F
D3
110 °C
230 °F
D5
110 °C
230 °F
D1
Roll Temperature 60.0 °C
140 °F
3rd
80.0 °C
176 °F
2nd
90.0 °C
194 °F
1st