Kraiburg TPE THERMOLAST® K TC6HAA Natural TPE  (Unverified Data**)

Category Polymer , Thermoplastic , Elastomer, TPE , Styrenic TPE
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kraiburg TPE THERMOLAST® K TC6HAA Natural TPE  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Adhesion to POM (Hostaform®, Duracon, Celcon)Patented system for TPE-S and POMEasy processabilityBroad service temperature rangeTypical Applications: Hard/soft applications with POM:SealingOver molded housingsFunctional ElementsDesign elementsMaterial Advantages: Excellent adhesion without pretreatment (depending on geometry and processing)Natural compounds easy to colorTactile surface (soft touch)Excellent flow characteristicsProcessing: Processing on 2K injection molding machines (many grades also for insert molding)Low back pressureHigh shear force is beneficial for flow behaviorHigh injection speed and pressureEasy demoldingInformation provided by Kraiburg TPE.
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
DIN EN ISO 1183-1:2004
Mechanical Properties Metric English Comments
Hardness, Shore A 57
57
DIN 53505/ISO 868
Tensile Strength at Break 3.80 MPa
551 psi
Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504/ ISO 37
Elongation at Break 530 %
530 %
Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504/ ISO 37
Tear Strength 18.0 kN/m
103 pli
ISO 34-1 method B (b)
Compression Set 29 %

@Temperature 23.0 °C,
Time 259000 sec
29 %

@Temperature 73.4 °F,
Time 72.0 hour
ISO 815
79 %

@Temperature 70.0 °C,
Time 79200 sec
79 %

@Temperature 158 °F,
Time 22.0 hour
ISO 815
87 %

@Temperature 100 °C,
Time 79200 sec
87 %

@Temperature 212 °F,
Time 22.0 hour
ISO 815
Processing Properties Metric English Comments
Processing Temperature 215 - 270 °C
419 - 518 °F
Mold Temperature 80.0 - 110 °C
176 - 230 °F
Drying Temperature 60.0 - 80.0 °C
140 - 176 °F
Pre-drying
Dry Time 2 - 4 hour
2 - 4 hour
Pre-drying
Descriptive Properties Value Comments
Color Natural