Kraton® D1116 K (SBS) Radial Triblock Copolymer
| Category | Polymer , Thermoplastic , Styrene-Butadiene , Styrene/Butadiene/Styrene (SBS) |
| Manufacturer | Kraton |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kraton® D1116 K (SBS) Radial Triblock Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Kraton D1116 K is a clear, radial triblock copolymer based on styrene and butadiene, with a polystyrene content of 23%. It is supplied from North America in the physical form identified: Kraton D1116 KT - supplied as a dusted porous pelletKraton D1116 KU - supplied as an undusted porous pelletKraton D1116 KIM - supplied as a dusted powderRegion: Asia Pacific, Europe, Japan, North America, and South America Uses: Kraton D1116 K is used as a modifier of bitumen or thermoplastics and in compound formulations. It is also suitable as an ingredient in formulating compounds for footwear applications and may be used in formulating adhesives, sealants and coatings.Applications: Adhesives, Sealant and Coatings; Bitumen Modification; Compounding and Personal Hygiene; Footwear; Impact Modification; Medical; Packaging and Polymod; Personal Care; and Roads and RoofingNote 1) The final dusting level is a combination of the talc from the original D1116 KT plus PGA-SD Alumina added during the milling processInformation provided by Kraton®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.940 g/cc | 0.940 g/cc | ASTM D4025 |
| Volatiles | <= 0.70 % | <= 0.70 % | KM 04 |
| Viscosity | 2000 - 3000 cP | 2000 - 3000 cP | 20% Toluene Solution at 25°C; BAM 922 |
| Melt Flow | <= 1.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
<= 1.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
|
| Ash | 0.15 - 0.35 % | 0.15 - 0.35 % | KT, Talc; BAM 908 |
| 3.0 - 5.0 % | 3.0 - 5.0 % | TIM, See Note 1); BAM 908 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 63 @Time 10.0 sec |
63 @Time 0.00278 hour |
Typical values on polymer compression molded at 350°F; ASTM D2240 |
| Tensile Strength | 31.7 MPa | 4600 psi | Typical properties of film cast from toluene solution; ASTM D412 |
| Elongation at Break | 900 % | 900 % | Typical properties of film cast from toluene solution; ASTM D412 |
| 300% Modulus | 0.00241 GPa | 0.350 ksi | Typical properties of film cast from toluene solution; ASTM D412 |
| Chemical Properties | Metric | English | Comments |
|---|---|---|---|
| Diblock Content | 16 % | 16 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Content | Non-staining phenolic antioxidant | 0.15-0.4%, KM 08 |
| Polystyrene | 21.1-24.4%, KM 03 | |
| Total Extractables | <1.0%, KM 05 | |
| Styrene/Rubber Ratio | 23/77 |