Kraton® D2109 DS-N (SBS) Compound
| Category | Polymer , Thermoplastic , Styrene-Butadiene , Styrene/Butadiene/Styrene (SBS) |
| Manufacturer | Kraton |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kraton® D2109 DS-N (SBS) Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Kraton D2109 DS-N is an easy processing, general purpose 45 Shore A hardness material designed for a wide variety of applications. It is supplied from North America in the physical form identified: Kraton D2109 DS-N - supplied as a translucent dense pelletRegion: North America, Europe, Asia Pacific, Japan, and South AmericaApplications: Adhesives, Sealant and Coatings; Bitumen Modification; Compounding and Personal Hygiene; Footwear; and Impact ModificationInformation provided by Kraton®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.915 - 0.945 g/cc | 0.915 - 0.945 g/cc | BAM 1014 |
| Linear Mold Shrinkage, Flow | 0.025 - 0.027 cm/cm | 0.025 - 0.027 in/in | |
| Melt Flow | 15 - 30 g/10 min @Load 5.00 kg, Temperature 200 °C |
15 - 30 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 40 - 50 | 40 - 50 | Value of product compression molded 120°C; BAM 1003 |
| Tensile Strength | 3.45 MPa | 500 psi | Machine Direction, typical properties Injection molded plaques, Die C; ASTM D412 |
| 4.83 MPa | 701 psi | Transverse Direction, typical properties Injection molded plaques, Die C; ASTM D412 | |
| Elongation at Break | 550 % | 550 % | Machine Direction, typical properties Injection molded plaques, Die C; ASTM D412 |
| 800 % | 800 % | Transverse Direction, typical properties Injection molded plaques, Die C; ASTM D412 | |
| 100% Modulus | 0.00103 GPa | 0.149 ksi | Transverse Direction, typical properties Injection molded plaques, Die C; ASTM D412 |
| 0.00138 GPa | 0.200 ksi | Machine Direction, typical properties Injection molded plaques, Die C; ASTM D412 | |
| 300% Modulus | 0.00172 GPa | 0.249 ksi | Transverse Direction, typical properties Injection molded plaques, Die C; ASTM D412 |
| 0.00207 GPa | 0.300 ksi | Machine Direction, typical properties Injection molded plaques, Die C; ASTM D412 | |
| Tear Strength | 21.9 kN/m | 125 pli | Transverse Direction, typical properties Injection molded plaques, Die C; ASTM D412 |
| 26.3 kN/m | 150 pli | Machine Direction, typical properties Injection molded plaques, Die C; ASTM D412 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 171 - 182 °C | 340 - 360 °F | |
| Middle Barrel Temperature | 177 - 193 °C | 350 - 380 °F | |
| Front Barrel Temperature | 188 - 199 °C | 370 - 390 °F | |
| Mold Temperature | 10.0 - 37.8 °C | 50.0 - 100 °F | |
| Injection Pressure | 3.549 - 4.928 MPa | 514.7 - 714.7 psi | |
| Back Pressure | 0.276 - 0.414 MPa | 40.0 - 60.0 psi |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-FLEX 602B Catalyst
- SABIC Innovative Plastics Lexan® HPS1 PC
- SABIC Innovative Plastics Lexan® XHT1143 PC (Asia Pacific)
- Overview of materials for Polyimide
- Johnson Matthey HPP Platinum Jewelry Alloy
- DuPont Vamac® GXF Sample Compound Vulcanizate Slab Cure (5 minutes at 190°C) Without Armeen® 18D
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 410, Hardened + 482°C Temper
Copyright © lookpolymers.com All Rights Reserved