Kraton® G1702 H (SEP) DiBlock Copolymer

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer Kraton
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kraton® G1702 H (SEP) DiBlock Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Kraton G1702 H is a clear, linear diblock copolymer based on styrene and ethylene/propylene with a polystyrene content of 28%. It is supplied from North America in the physical form identified: Kraton G1702 HU - supplied as a powder.Region: Asia Pacific, Europe, Japan, North America, and South America Uses: Kraton G1702 H is used as an ingredient in formulating adhesives, sealants and coatings. It may also find use as a modifier of bitumen or thermoplastics and in compound formulations.Applications: Adhesives, Sealant and Coatings; Compounding and Personal Hygiene; Packaging and Polymod; and Personal Care
Physical Properties Metric English Comments
Specific Gravity 0.910 g/cc
0.910 g/cc
ASTM D4025
Volatiles <= 0.40 %
<= 0.40 %
KM 04
Kinematic Viscosity at 100°C (212°F) 18 - 22 cSt
18 - 22 cSt
1.23%; BAM 1201
Melt Flow <= 1.0 g/10 min

@Load 5.00 kg,
Temperature 230 °C
<= 1.0 g/10 min

@Load 11.0 lb,
Temperature 446 °F
Mechanical Properties Metric English Comments
Hardness, Shore A 41
41
10 seconds. Typical values on polymer compression molded at 350°F; ASTM D2240
Tensile Strength, Ultimate 2.068 MPa
299.9 psi
Typical properties based on film cast from toluene solution.; ASTM D412
Elongation at Break <= 100 %
<= 100 %
Typical properties based on film cast from toluene solution.; ASTM D412
Chemical Properties Metric English Comments
Diblock Content 100 %
100 %
Descriptive Properties Value Comments
Content Non-staining phenolic antioxidant
0.03-0.2%, KM 08
Polystyrene
26.2-29%, KM 03, Measured on the polymer before hydrogenation
Styrene/Rubber Ratio 28/72