Kuraray Genestarâ„¢ G1301A-M61 Nylon, 30% Glass Filled
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Kuraray Company |
| Trade Name | Genestar™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kuraray Genestarâ„¢ G1301A-M61 Nylon, 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass reinforced and impact modified injection grade.Main Features:Higher elongation and impact strengthHeat resistanceChemical resistanceExample of applications:Quick connector
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | |
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Water Absorption | 0.19 % | 0.19 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 175 MPa | 25400 psi | ISO 527-1/-2 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| Tensile Modulus | 8.98 GPa | 1300 ksi | ISO 527-1/-2 |
| Flexural Strength | 250 MPa | 36300 psi | ISO 178 |
| Flexural Modulus | 8.20 GPa | 1190 ksi | ISO 178 |
| Charpy Impact, Notched | 1.70 J/cm² | 8.09 ft-lb/in² | ISO 179/1eA |
| Coefficient of Friction | 0.30 | 0.30 | ISO JIS K7218-A |
| K Factor (Wear Factor) | 15 | 15 | [mg] |
| Limiting Pressure Velocity | 0.980 MPa-m/sec | 28000 psi-ft/min |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ASTM D696 |
| CTE, linear, Transverse to Flow | 46.0 µm/m-°C | 25.6 µin/in-°F | ASTM D696 |
| Melting Point | 300 °C | 572 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C | 518 °F | ISO 75-1/-2 |
| Glass Transition Temp, Tg | 125 °C | 257 °F | 10°C/min; ISO 11357-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Lubricants | |
| Release Agent | ||
| Applications | Automotive | |
| General Purpose | ||
| Chemical Resistance | Acid Resistance | |
| Alkali Resistance | ||
| Environmental Stress Crack Resistance | ||
| General Chemical Resistance | ||
| Grease Resistance | ||
| Hydrolytically Stable | ||
| Oil Resistance | ||
| Solvent Resistance | ||
| Delivery Form | Black | |
| Other Features | Barrier Properties | |
| Creep Resistance | ||
| High Crystalinity | ||
| Low Coefficient of Friction | ||
| Thermal Stability | ||
| Weldable | ||
| Regional Availability | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America | ||
| Special Characteristics | Heat Stabilized or Stable to Heat | |
| High Impact or Impact Modified |