- Kuraray Genestarâ„¢ GW2458HF Nylon, 45% Glass Filled
Kuraray Genestarâ„¢ GW2458HF Nylon, 45% Glass Filled
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Kuraray Company |
| Trade Name | Genestar™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kuraray Genestarâ„¢ GW2458HF Nylon, 45% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Low Warpage, High Flow V-0 Grade. It is suited for low warpage and high flow applications, making it well suited for card connectors.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.73 g/cc | 1.73 g/cc | |
| Water Absorption | 0.80 % | 0.80 % | |
| Linear Mold Shrinkage, Flow | 0.00030 cm/cm | 0.00030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm | 0.0040 in/in | |
| Melt Flow | 84 g/10 min @Load 2.16 kg, Temperature 320 °C |
84 g/10 min @Load 4.76 lb, Temperature 608 °F |
ASTM D1238 |
| Spiral Flow | 7.10 cm @Load 750 kg, Temperature 320 °C |
2.80 in @Load 1650 lb, Temperature 608 °F |
0.5mm diameter |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 35.0 MPa | 5080 psi | Weld; ASTM D638 |
| 165 MPa | 23900 psi | ASTM D638 | |
| Elongation at Yield | 0.30 % | 0.30 % | Weld; ASTM D638 |
| 3.5 % | 3.5 % | ASTM D638 | |
| Flexural Strength | 225 MPa | 32600 psi | ASTM D790 |
| Flexural Modulus | 15.0 GPa | 2180 ksi | ASTM D790 |
| Izod Impact, Notched | 1.25 J/cm | 2.34 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 306 °C | 583 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | ASTM D648 |
| Glass Transition Temp, Tg | 125 °C | 257 °F | |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.8 @Frequency 1.00e+10 Hz |
3.8 @Frequency 1.00e+10 Hz |
ASTM D150 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | ASTM D149 |
| Dielectric Loss Index | 0.010 @Frequency 1.00e+10 Hz |
0.010 @Frequency 1.00e+10 Hz |
ASTM D150 |
| Comparative Tracking Index | >= 600 V | >= 600 V | ASTM UL746A |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylex® P1310FRMA Polycarbonate
- PolyOne Geon™ L4605 Ivory 3098 Polyvinyl Chloride, Semi-Rigid (PVC, Semi-Rigid)
- Lehmann & Voss Nylatron® MR 2007 Polyamide 6, with mineral filler
- Momentive Performance Materials Addisilâ„¢ 472 E Healthcare Extrusion Grade Heat Cured Rubber
- Techmer ES HiFill FR® PC FR X
- Techmer ES HiFill® PEEK CF20 TL15 HF 20% Carbon Filled
- Zell-Metall Engineering Plastics Zellamid 1115 at 50% RH
- 3M Scotch-Weld™ 1357-L Neoprene High Performance Contact Adhesive
- BASF Ultramid® B3ZG3 15% Glass Filled PA6 (Dry)
- Chang Chun Plastic PBT2100 Fire Retardant PBT
Copyright © lookpolymers.com All Rights Reserved