LATI Kelon® B FR H2 CE/25-V2HF PA 6, Mineral Reinforced, Flame Retardant, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer LATI
Trade Name Kelon® B
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Kelon® B FR H2 CE/25-V2HF PA 6, Mineral Reinforced, Flame Retardant, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 6 (PA6) based compound. Heat stabilized. Mineral filler. UL94 V-2 classified, halogens-based flame retardants and red phosphorous free.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
Linear Mold Shrinkage, Flow 0.0055 - 0.0075 cm/cm
0.0055 - 0.0075 in/in
Linear Mold Shrinkage, Transverse 0.0065 - 0.0085 cm/cm
0.0065 - 0.0085 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 15.0 MPa

@Temperature 150 °C
 2180 psi

@Temperature 302 °F
20.0 MPa

@Temperature 120 °C
 2900 psi

@Temperature 248 °F
30.0 MPa

@Temperature 90.0 °C
 4350 psi

@Temperature 194 °F
45.0 MPa

@Temperature 60.0 °C
 6530 psi

@Temperature 140 °F
65.0 MPa

@Temperature 23.0 °C
 9430 psi

@Temperature 73.4 °F
Elongation at Break 2.5 %

@Temperature 23.0 °C
 2.5 %

@Temperature 73.4 °F
3.5 %

@Temperature 60.0 °C
 3.5 %

@Temperature 140 °F
6.5 %

@Temperature 90.0 °C
 6.5 %

@Temperature 194 °F
12 %

@Temperature 120 °C
 12 %

@Temperature 248 °F
20 %

@Temperature 150 °C
 20 %

@Temperature 302 °F
Tensile Modulus 0.500 GPa

@Temperature 150 °C
 72.5 ksi

@Temperature 302 °F
0.750 GPa

@Temperature 120 °C
 109 ksi

@Temperature 248 °F
1.30 GPa

@Temperature 90.0 °C
 189 ksi

@Temperature 194 °F
2.20 GPa

@Temperature 60.0 °C
 319 ksi

@Temperature 140 °F
5.20 GPa

@Temperature 23.0 °C
 754 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 3.00 J/cm²
14.3 ft-lb/in²
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 80.0 °C
176 °F
Deflection Temperature at 0.46 MPa (66 psi) 200 °C
392 °F
Deflection Temperature at 1.8 MPa (264 psi) 120 °C
248 °F
Vicat Softening Point 205 °C

@Load 5.00 kg
 401 °F

@Load 11.0 lb
Flammability, UL94 V-2

@Thickness 3.00 mm
 V-2

@Thickness 0.118 in
V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0591 in
V-2

@Thickness 0.750 mm
 V-2

@Thickness 0.0295 in
Oxygen Index 27 %
27 %
Glow Wire Test 960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 550 V
550 V
A solution
Processing Properties Metric English Comments
Melt Temperature 240 - 260 °C
464 - 500 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa