LATI LARPEEK 50 G/50 50% Glass Reinforced Polyetheretherketone (PEEK)  (discontinued **)

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI LARPEEK 50 G/50 50% Glass Reinforced Polyetheretherketone (PEEK)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Larpeek polyetheretherketone (PEEK) is a high performance thermoplastic offering cost effective performance in difficult environments across all industries. PEEK is temperature resistant (up to 250°C), offers outstanding wear performance and has a comprehensive resistance to chemicals and aggressive agents. Larpeek compounds are intrinsically flame retardant and maintain UL94 V0 rating in thin walled products without requiring any special additive. Larpeek compounds can substitute metals, ceramics, and composites in many engineering applications offering improved performance together with simplified production, reduced cost and extended reliability.Specific Notes for this Material: PEEK, 50% glass fiber, flame retardant UL94 V0, halogens and red phosphorous freeDisclaimer from LATI: This document contains information based on average values as obtained from the results of laboratory tests and observations made on LATI materials. Tested materials were injection molded, used in their natural color, and conditioned in compliance with Standard ASTM D 618, procedure A. These values refer to LATI's best technical and scientific knowledge at the moment of testing and cannot be used as a basis for the development of applications. For a better assessment of the materials, you are kindly requested to contact LATI's technical or commercial offices, which are at your disposal and will supply detailed information on the most suitable characteristics for their intended use. With reference to DPR n.224 dated May 24, 1988, issued in accordance with EC Guide-lines 85/374, LATI Industria Termoplastici S.p.A. declines all responsibility arising from an improper use of the products described in this document.All data provided by LATI.
Physical Properties Metric English Comments
Density 1.70 g/cc
0.0614 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
LATI
Linear Mold Shrinkage, Transverse 0.0055 cm/cm
0.0055 in/in
LATI
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 225 MPa
32600 psi
ISO 527
Flexural Modulus 16.0 GPa
2320 ksi
ASTM D790
Izod Impact, Notched 1.08 J/cm

@Temperature 23.0 °C
2.02 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) >= 300 °C
>= 572 °F
ASTM D648
Flammability, UL94 V-0

@Thickness 0.750 mm
V-0

@Thickness 0.0295 in
Processing Properties Metric English Comments
Melt Temperature 380 - 400 °C
716 - 752 °F
Mold Temperature 180 - 190 °C
356 - 374 °F
Drying Temperature 150 - 170 °C
302 - 338 °F
Always recommended, temperature can be reduced when using vacuum ovens.
Dry Time >= 3 hour
>= 3 hour
Always recommended, drying time can be reduced when using vacuum ovens.
Descriptive Properties Value Comments
Injection Speed medium