LATI LATILUB 88/50-20GRT K/10 PEEK Based, 10% Carbon Fiber Reinforced, 20% Graphite and PTFE Self Lubricating Plastic

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI LATILUB 88/50-20GRT K/10 PEEK Based, 10% Carbon Fiber Reinforced, 20% Graphite and PTFE Self Lubricating Plastic.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Latilub self-lubricating plastic materials are designed to replace metals in applications such as gears, bushings, cams, slides, etc., for which, besides their intrinsic properties (moldability, low cost, lightness, high mechanical properties), low friction coefficient and low wear are required.Specific Notes for this Material: PEEK, 10% carbon fiber, 20% graphite and PTFE, flame retardant UL94 V0, halogens and red phosphorous freeDisclaimer from LATI: This document contains information based on average values as obtained from the results of laboratory tests and observations made on LATI materials. Tested materials were injection molded, used in their natural color, and conditioned in compliance with Standard ASTM D 618, procedure A. These values refer to LATI's best technical and scientific knowledge at the moment of testing and cannot be used as a basis for the development of applications. For a better assessment of the materials, you are kindly requested to contact LATI's technical or commercial offices, which are at your disposal and will supply detailed information on the most suitable characteristics for their intended use. With reference to DPR n.224 dated May 24, 1988, issued in accordance with EC Guide-lines 85/374, LATI Industria Termoplastici S.p.A. declines all responsibility arising from an improper use of the products described in this document.All data provided by LATI.
Physical Properties Metric English Comments
Density 1.44 g/cc
0.0520 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
LATI
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
LATI
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 120 MPa
17400 psi
ISO 527
Flexural Modulus 8.80 GPa
1280 ksi
ASTM D790
Izod Impact, Notched 0.570 J/cm

@Temperature 23.0 °C
1.07 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
ASTM D648
Flammability, UL94 V-0

@Thickness 0.750 mm
V-0

@Thickness 0.0295 in
Processing Properties Metric English Comments
Melt Temperature 365 - 385 °C
689 - 725 °F
Mold Temperature 180 - 190 °C
356 - 374 °F
Drying Temperature 150 - 170 °C
302 - 338 °F
Always recommended, temperature can be reduced when using vacuum ovens.
Dry Time >= 3 hour
>= 3 hour
Always recommended, drying time can be reduced when using vacuum ovens.
Descriptive Properties Value Comments
Injection Speed medium