LATI Lapex R G/20 PPSU, 20% Glass Reinforced

Category Polymer , Thermoplastic , Polyphenylsulfone (PPSU)
Manufacturer LATI
Trade Name Lapex
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Lapex R G/20 PPSU, 20% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyphenylene Sulfone (PPSU) based compound. Glass fibers. Low smoke density and low toxicity index. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
Linear Mold Shrinkage, Flow 0.0040 - 0.0055 cm/cm
0.0040 - 0.0055 in/in
Linear Mold Shrinkage, Transverse 0.0080 - 0.0095 cm/cm
0.0080 - 0.0095 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.0 MPa

@Temperature 150 °C
 9430 psi

@Temperature 302 °F
85.0 MPa

@Temperature 120 °C
 12300 psi

@Temperature 248 °F
95.0 MPa

@Temperature 90.0 °C
 13800 psi

@Temperature 194 °F
105 MPa

@Temperature 60.0 °C
 15200 psi

@Temperature 140 °F
110 MPa

@Temperature 23.0 °C
 16000 psi

@Temperature 73.4 °F
Elongation at Break 2.1 %

@Temperature 150 °C
 2.1 %

@Temperature 302 °F
2.2 %

@Temperature 60.0 °C
 2.2 %

@Temperature 140 °F
2.2 %

@Temperature 90.0 °C
 2.2 %

@Temperature 194 °F
2.2 %

@Temperature 120 °C
 2.2 %

@Temperature 248 °F
2.5 %

@Temperature 23.0 °C
 2.5 %

@Temperature 73.4 °F
Tensile Modulus 4.60 GPa

@Temperature 150 °C
 667 ksi

@Temperature 302 °F
4.80 GPa

@Temperature 120 °C
 696 ksi

@Temperature 248 °F
5.10 GPa

@Temperature 90.0 °C
 740 ksi

@Temperature 194 °F
5.60 GPa

@Temperature 60.0 °C
 812 ksi

@Temperature 140 °F
5.90 GPa

@Temperature 23.0 °C
 856 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 2.50 J/cm²
11.9 ft-lb/in²
Charpy Impact, Notched 1.50 J/cm²
7.14 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 190 °C
374 °F
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Vicat Softening Point 220 °C

@Load 5.00 kg
 428 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Oxygen Index 38 %
38 %
Processing Properties Metric English Comments
Melt Temperature 350 - 390 °C
662 - 734 °F
Mold Temperature 150 - 190 °C
302 - 374 °F
Drying Temperature 140 - 180 °C

@Time 10800 sec
 284 - 356 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa