LATI Laramid G/15 PPA, 15% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 20% Glass Fiber Reinforced
Manufacturer LATI
Trade Name Laramid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Laramid G/15 PPA, 15% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Semi-aromatic polyamide (PPA) based compound. Glass fibers. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
Linear Mold Shrinkage, Transverse 0.0085 - 0.0115 cm/cm
0.0085 - 0.0115 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa

@Temperature 150 °C
 7980 psi

@Temperature 302 °F
75.0 MPa

@Temperature 120 °C
 10900 psi

@Temperature 248 °F
100 MPa

@Temperature 90.0 °C
 14500 psi

@Temperature 194 °F
105 MPa

@Temperature 60.0 °C
 15200 psi

@Temperature 140 °F
110 MPa

@Temperature 23.0 °C
 16000 psi

@Temperature 73.4 °F
Elongation at Break 2.0 %

@Temperature 23.0 °C
 2.0 %

@Temperature 73.4 °F
2.0 %

@Temperature 60.0 °C
 2.0 %

@Temperature 140 °F
2.0 %

@Temperature 90.0 °C
 2.0 %

@Temperature 194 °F
5.0 %

@Temperature 120 °C
 5.0 %

@Temperature 248 °F
12 %

@Temperature 150 °C
 12 %

@Temperature 302 °F
Elongation at Yield 3.5 %

@Temperature 120 °C
 3.5 %

@Temperature 248 °F
10 %

@Temperature 150 °C
 10 %

@Temperature 302 °F
Tensile Modulus 2.00 GPa

@Temperature 150 °C
 290 ksi

@Temperature 302 °F
4.40 GPa

@Temperature 120 °C
 638 ksi

@Temperature 248 °F
5.70 GPa

@Temperature 90.0 °C
 827 ksi

@Temperature 194 °F
6.80 GPa

@Temperature 60.0 °C
 986 ksi

@Temperature 140 °F
7.20 GPa

@Temperature 23.0 °C
 1040 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 1.70 J/cm²

@Temperature -20.0 °C
 8.09 ft-lb/in²

@Temperature -4.00 °F
2.00 J/cm²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.400 J/cm²

@Temperature 23.0 °C
 1.90 ft-lb/in²

@Temperature 73.4 °F
0.400 J/cm²

@Temperature -20.0 °C
 1.90 ft-lb/in²

@Temperature -4.00 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 135 °C
275 °F
Deflection Temperature at 0.46 MPa (66 psi) 280 °C
536 °F
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
Vicat Softening Point 265 °C

@Load 5.00 kg
 509 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 310 - 330 °C
590 - 626 °F
Mold Temperature 150 - 170 °C
302 - 338 °F
Drying Temperature 120 - 130 °C

@Time 10800 sec
 248 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa