LATI Laramid G/60 PPA, 60% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer LATI
Trade Name Laramid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Laramid G/60 PPA, 60% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Semi-aromatic polyamide (PPA) based compound. Glass fibers. Very good thermal properties. Good chemical resistance. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.78 g/cc
0.0643 lb/in³
Linear Mold Shrinkage, Flow 0.0015 - 0.0035 cm/cm
0.0015 - 0.0035 in/in
Linear Mold Shrinkage, Transverse 0.0040 - 0.0065 cm/cm
0.0040 - 0.0065 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa

@Temperature 150 °C
 14500 psi

@Temperature 302 °F
165 MPa

@Temperature 120 °C
 23900 psi

@Temperature 248 °F
215 MPa

@Temperature 90.0 °C
 31200 psi

@Temperature 194 °F
240 MPa

@Temperature 60.0 °C
 34800 psi

@Temperature 140 °F
280 MPa

@Temperature 23.0 °C
 40600 psi

@Temperature 73.4 °F
Elongation at Break 1.8 %

@Temperature 23.0 °C
 1.8 %

@Temperature 73.4 °F
1.9 %

@Temperature 60.0 °C
 1.9 %

@Temperature 140 °F
2.2 %

@Temperature 90.0 °C
 2.2 %

@Temperature 194 °F
3.3 %

@Temperature 120 °C
 3.3 %

@Temperature 248 °F
5.0 %

@Temperature 150 °C
 5.0 %

@Temperature 302 °F
Tensile Modulus 6.50 GPa

@Temperature 150 °C
 943 ksi

@Temperature 302 °F
15.0 GPa

@Temperature 120 °C
 2180 ksi

@Temperature 248 °F
20.0 GPa

@Temperature 90.0 °C
 2900 ksi

@Temperature 194 °F
22.0 GPa

@Temperature 60.0 °C
 3190 ksi

@Temperature 140 °F
24.0 GPa

@Temperature 23.0 °C
 3480 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 9.00 J/cm²
42.8 ft-lb/in²
Charpy Impact, Notched 1.50 J/cm²
7.14 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 150 °C
302 °F
Deflection Temperature at 0.46 MPa (66 psi) 290 °C
554 °F
Deflection Temperature at 1.8 MPa (264 psi) 280 °C
536 °F
Vicat Softening Point 280 °C

@Load 5.00 kg
 536 °F

@Load 11.0 lb
Flammability, UL94 HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
Oxygen Index 42 %
42 %
Glow Wire Test 750 °C

@Thickness 1.00 mm
 1380 °F

@Thickness 0.0394 in
 GWFI/GWT
750 °C

@Thickness 2.00 mm
 1380 °F

@Thickness 0.0787 in
 GWFI/GWT
Processing Properties Metric English Comments
Melt Temperature 310 - 340 °C
590 - 644 °F
Mold Temperature 150 - 170 °C
302 - 338 °F
Drying Temperature 120 - 130 °C

@Time 10800 sec
 248 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa