LATI Laril 13 G/20-V1 PPOm, 20% Glass Fiber Reinforced, Flame Retardant

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 20% Glass Filled
Manufacturer LATI
Trade Name Laril
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Laril 13 G/20-V1 PPOm, 20% Glass Fiber Reinforced, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Modified Polyphenylene Oxide (PPOm) based compound. Glass fibers. UL94 V-1 classified, with brominated flame retardants, PBB/PBDE and antimony trioxide free. High dimensional stability. Good thermal properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
Linear Mold Shrinkage, Flow 0.0040 - 0.0065 cm/cm
0.0040 - 0.0065 in/in
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 20.0 MPa

@Temperature 120 °C
 2900 psi

@Temperature 248 °F
45.0 MPa

@Temperature 90.0 °C
 6530 psi

@Temperature 194 °F
70.0 MPa

@Temperature 60.0 °C
 10200 psi

@Temperature 140 °F
90.0 MPa

@Temperature 23.0 °C
 13100 psi

@Temperature 73.4 °F
Elongation at Break 2.0 %

@Temperature 23.0 °C
 2.0 %

@Temperature 73.4 °F
2.0 %

@Temperature 60.0 °C
 2.0 %

@Temperature 140 °F
2.2 %

@Temperature 90.0 °C
 2.2 %

@Temperature 194 °F
3.0 %

@Temperature 120 °C
 3.0 %

@Temperature 248 °F
Elongation at Yield 1.5 %

@Temperature 90.0 °C
 1.5 %

@Temperature 194 °F
1.5 %

@Temperature 120 °C
 1.5 %

@Temperature 248 °F
Tensile Modulus 3.30 GPa

@Temperature 120 °C
 479 ksi

@Temperature 248 °F
5.40 GPa

@Temperature 90.0 °C
 783 ksi

@Temperature 194 °F
6.00 GPa

@Temperature 60.0 °C
 870 ksi

@Temperature 140 °F
6.90 GPa

@Temperature 23.0 °C
 1000 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 2.50 J/cm²

@Temperature 23.0 °C
 11.9 ft-lb/in²

@Temperature 73.4 °F
2.50 J/cm²

@Temperature -20.0 °C
 11.9 ft-lb/in²

@Temperature -4.00 °F
Charpy Impact, Notched 0.600 J/cm²

@Temperature -20.0 °C
 2.86 ft-lb/in²

@Temperature -4.00 °F
0.700 J/cm²

@Temperature 23.0 °C
 3.33 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 115 °C
239 °F
Deflection Temperature at 0.46 MPa (66 psi) 130 °C
266 °F
Deflection Temperature at 1.8 MPa (264 psi) 125 °C
257 °F
Vicat Softening Point 130 °C

@Load 5.00 kg
 266 °F

@Load 11.0 lb
Flammability, UL94 V-1

@Thickness 1.50 mm
 V-1

@Thickness 0.0591 in
Oxygen Index 31 %
31 %
Glow Wire Test 960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 250 V
250 V
A solution
Processing Properties Metric English Comments
Melt Temperature 260 - 280 °C
500 - 536 °F
Mold Temperature 80.0 - 90.0 °C
176 - 194 °F
Drying Temperature 80.0 - 90.0 °C

@Time 10800 sec
 176 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa