LATI Larton GK/400 PPS, Glass/Carbon Fiber Reinforced

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer LATI
Trade Name Larton
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Larton GK/400 PPS, Glass/Carbon Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyphenylene Sulfide (PPS) based compound. Glass fibers / Carbon fibers. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.59 g/cc
0.0574 lb/in³
Linear Mold Shrinkage, Flow 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
Linear Mold Shrinkage, Transverse 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 85.0 MPa

@Temperature 150 °C
 12300 psi

@Temperature 302 °F
105 MPa

@Temperature 120 °C
 15200 psi

@Temperature 248 °F
155 MPa

@Temperature 90.0 °C
 22500 psi

@Temperature 194 °F
170 MPa

@Temperature 60.0 °C
 24700 psi

@Temperature 140 °F
190 MPa

@Temperature 23.0 °C
 27600 psi

@Temperature 73.4 °F
Elongation at Break 1.1 %

@Temperature 23.0 °C
 1.1 %

@Temperature 73.4 °F
1.1 %

@Temperature 60.0 °C
 1.1 %

@Temperature 140 °F
1.3 %

@Temperature 90.0 °C
 1.3 %

@Temperature 194 °F
1.7 %

@Temperature 120 °C
 1.7 %

@Temperature 248 °F
1.8 %

@Temperature 150 °C
 1.8 %

@Temperature 302 °F
Tensile Modulus 9.00 GPa

@Temperature 150 °C
 1310 ksi

@Temperature 302 °F
11.4 GPa

@Temperature 120 °C
 1650 ksi

@Temperature 248 °F
17.7 GPa

@Temperature 90.0 °C
 2570 ksi

@Temperature 194 °F
19.3 GPa

@Temperature 60.0 °C
 2800 ksi

@Temperature 140 °F
22.0 GPa

@Temperature 23.0 °C
 3190 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 3.00 J/cm²
14.3 ft-lb/in²
Charpy Impact, Notched 0.550 J/cm²
2.62 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 225 °C
437 °F
Deflection Temperature at 0.46 MPa (66 psi) 280 °C
536 °F
Deflection Temperature at 1.8 MPa (264 psi) 265 °C
509 °F
Vicat Softening Point 260 °C

@Load 5.00 kg
 500 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 290 - 320 °C
554 - 608 °F
Mold Temperature 130 - 140 °C
266 - 284 °F
Drying Temperature 130 - 150 °C

@Time 10800 sec
 266 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa