LATI Lastil G/30 SAN, 30% Glass Fiber Reinforced

Category Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded, Glass Reinforced
Manufacturer LATI
Trade Name Lastil
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Lastil G/30 SAN, 30% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Styrene-Acrylonitrile copolymer (SAN) based compound. Glass fibers. High dimensional stability. High stiffness.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
Linear Mold Shrinkage, Flow 0.0015 - 0.0030 cm/cm
0.0015 - 0.0030 in/in
Linear Mold Shrinkage, Transverse 0.0025 - 0.0045 cm/cm
0.0025 - 0.0045 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 25.0 MPa

@Temperature 90.0 °C
3630 psi

@Temperature 194 °F
60.0 MPa

@Temperature 60.0 °C
8700 psi

@Temperature 140 °F
80.0 MPa

@Temperature 23.0 °C
11600 psi

@Temperature 73.4 °F
Elongation at Break 2.0 %

@Temperature 23.0 °C
2.0 %

@Temperature 73.4 °F
2.0 %

@Temperature 60.0 °C
2.0 %

@Temperature 140 °F
2.5 %

@Temperature 90.0 °C
2.5 %

@Temperature 194 °F
Elongation at Yield 1.2 %

@Temperature 90.0 °C
1.2 %

@Temperature 194 °F
Tensile Modulus 6.00 GPa

@Temperature 90.0 °C
870 ksi

@Temperature 194 °F
8.00 GPa

@Temperature 60.0 °C
1160 ksi

@Temperature 140 °F
9.60 GPa

@Temperature 23.0 °C
1390 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 1.00 J/cm²

@Temperature -20.0 °C
4.76 ft-lb/in²

@Temperature -4.00 °F
1.20 J/cm²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.250 J/cm²

@Temperature 23.0 °C
1.19 ft-lb/in²

@Temperature 73.4 °F
0.300 J/cm²

@Temperature -20.0 °C
1.43 ft-lb/in²

@Temperature -4.00 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 95.0 °C
203 °F
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
Deflection Temperature at 1.8 MPa (264 psi) 100 °C
212 °F
Vicat Softening Point 110 °C

@Load 5.00 kg
230 °F

@Load 11.0 lb
Oxygen Index 22 %
22 %
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
A solution
Processing Properties Metric English Comments
Melt Temperature 220 - 260 °C
428 - 500 °F
Mold Temperature 50.0 - 70.0 °C
122 - 158 °F
Drying Temperature 70.0 - 80.0 °C

@Time 10800 sec
158 - 176 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa