Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced
Manufacturer LATI
Trade Name Lastilac
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Lastilac 10 ABS/PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ABS/PC Blend (ABS/PC). Unfilled. Very good surface appearance. High impact resistance. Good thermal properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.12 g/cc
0.0405 lb/in³
Linear Mold Shrinkage, Flow 0.0055 - 0.0075 cm/cm
0.0055 - 0.0075 in/in
Linear Mold Shrinkage, Transverse 0.0055 - 0.0075 cm/cm
0.0055 - 0.0075 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 20.0 MPa

@Temperature 90.0 °C
 2900 psi

@Temperature 194 °F
45.0 MPa

@Temperature 60.0 °C
 6530 psi

@Temperature 140 °F
55.0 MPa

@Temperature 23.0 °C
 7980 psi

@Temperature 73.4 °F
Elongation at Break 40 %

@Temperature 23.0 °C
 40 %

@Temperature 73.4 °F
45 %

@Temperature 60.0 °C
 45 %

@Temperature 140 °F
55 %

@Temperature 90.0 °C
 55 %

@Temperature 194 °F
Elongation at Yield 4.0 %

@Temperature 60.0 °C
 4.0 %

@Temperature 140 °F
5.0 %

@Temperature 23.0 °C
 5.0 %

@Temperature 73.4 °F
6.0 %

@Temperature 90.0 °C
 6.0 %

@Temperature 194 °F
Tensile Modulus 1.90 GPa

@Temperature 90.0 °C
 276 ksi

@Temperature 194 °F
2.20 GPa

@Temperature 60.0 °C
 319 ksi

@Temperature 140 °F
2.50 GPa

@Temperature 23.0 °C
 363 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
Charpy Impact, Notched 6.50 J/cm²

@Temperature 23.0 °C
 30.9 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 75.0 °C
167 °F
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
Deflection Temperature at 1.8 MPa (264 psi) 105 °C
221 °F
Vicat Softening Point 110 °C

@Load 5.00 kg
 230 °F

@Load 11.0 lb
Oxygen Index 25 %
25 %
Electrical Properties Metric English Comments
Comparative Tracking Index 250 V
250 V
A solution
Processing Properties Metric English Comments
Melt Temperature 230 - 250 °C
446 - 482 °F
Mold Temperature 50.0 - 70.0 °C
122 - 158 °F
Drying Temperature 80.0 - 100 °C

@Time 10800 sec
 176 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa