LATI Lasulf G/30 PSU, 30% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polysulfone (PSU) , Polysulfone, 30% Glass Fiber Reinforced
Manufacturer LATI
Trade Name Lasulf
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Lasulf G/30 PSU, 30% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polysulfone (PSU) based compound. Glass fibers. Low smoke density and low toxicity index. Very high dimensional stabilityAvailability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.47 g/cc
0.0531 lb/in³
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
Linear Mold Shrinkage, Transverse 0.0045 - 0.0060 cm/cm
0.0045 - 0.0060 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.0 MPa

@Temperature 150 °C
 10200 psi

@Temperature 302 °F
80.0 MPa

@Temperature 120 °C
 11600 psi

@Temperature 248 °F
95.0 MPa

@Temperature 90.0 °C
 13800 psi

@Temperature 194 °F
110 MPa

@Temperature 60.0 °C
 16000 psi

@Temperature 140 °F
120 MPa

@Temperature 23.0 °C
 17400 psi

@Temperature 73.4 °F
Elongation at Break 1.6 %

@Temperature 150 °C
 1.6 %

@Temperature 302 °F
1.7 %

@Temperature 120 °C
 1.7 %

@Temperature 248 °F
1.8 %

@Temperature 60.0 °C
 1.8 %

@Temperature 140 °F
1.8 %

@Temperature 90.0 °C
 1.8 %

@Temperature 194 °F
1.9 %

@Temperature 23.0 °C
 1.9 %

@Temperature 73.4 °F
Tensile Modulus 7.00 GPa

@Temperature 150 °C
 1020 ksi

@Temperature 302 °F
7.30 GPa

@Temperature 120 °C
 1060 ksi

@Temperature 248 °F
7.50 GPa

@Temperature 90.0 °C
 1090 ksi

@Temperature 194 °F
7.70 GPa

@Temperature 60.0 °C
 1120 ksi

@Temperature 140 °F
8.00 GPa

@Temperature 23.0 °C
 1160 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 3.50 J/cm²
16.7 ft-lb/in²
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 160 °C
320 °F
Deflection Temperature at 0.46 MPa (66 psi) 190 °C
374 °F
Deflection Temperature at 1.8 MPa (264 psi) 185 °C
365 °F
Vicat Softening Point 185 °C

@Load 5.00 kg
 365 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Oxygen Index 38 %
38 %
Glow Wire Test 960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 125 V
125 V
A solution
Processing Properties Metric English Comments
Melt Temperature 300 - 330 °C
572 - 626 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Drying Temperature 110 - 130 °C

@Time 10800 sec
 230 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa