LATI Latamid 6 H2 G/55 PA 6, 55% Glass Fiber Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 60% Glass Fiber Filled
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 6 H2 G/55 PA 6, 55% Glass Fiber Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.62 g/cc
0.0585 lb/in³
Linear Mold Shrinkage, Flow 0.0020 - 0.0045 cm/cm
0.0020 - 0.0045 in/in
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 105 MPa

@Temperature 150 °C
 15200 psi

@Temperature 302 °F
120 MPa

@Temperature 120 °C
 17400 psi

@Temperature 248 °F
135 MPa

@Temperature 90.0 °C
 19600 psi

@Temperature 194 °F
165 MPa

@Temperature 60.0 °C
 23900 psi

@Temperature 140 °F
220 MPa

@Temperature 23.0 °C
 31900 psi

@Temperature 73.4 °F
Elongation at Break 2.5 %

@Temperature 23.0 °C
 2.5 %

@Temperature 73.4 °F
2.9 %

@Temperature 60.0 °C
 2.9 %

@Temperature 140 °F
3.6 %

@Temperature 90.0 °C
 3.6 %

@Temperature 194 °F
4.0 %

@Temperature 120 °C
 4.0 %

@Temperature 248 °F
4.4 %

@Temperature 150 °C
 4.4 %

@Temperature 302 °F
Tensile Modulus 6.20 GPa

@Temperature 150 °C
 899 ksi

@Temperature 302 °F
7.60 GPa

@Temperature 120 °C
 1100 ksi

@Temperature 248 °F
9.30 GPa

@Temperature 90.0 °C
 1350 ksi

@Temperature 194 °F
13.7 GPa

@Temperature 60.0 °C
 1990 ksi

@Temperature 140 °F
17.0 GPa

@Temperature 23.0 °C
 2470 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 8.50 J/cm²
40.4 ft-lb/in²
Charpy Impact, Notched 1.50 J/cm²
7.14 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 130 °C
266 °F
Deflection Temperature at 0.46 MPa (66 psi) 225 °C
437 °F
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
Vicat Softening Point 220 °C

@Load 5.00 kg
 428 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 240 - 280 °C
464 - 536 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa