LATI Latamid 6 H2PX-V0 PA 6, Heat Stabilized, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 6 H2PX-V0 PA 6, Heat Stabilized, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 6 (PA6) based compound. Heat stabilized. Toughened. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
Linear Mold Shrinkage, Flow 0.011 - 0.0145 cm/cm
0.011 - 0.0145 in/in
Linear Mold Shrinkage, Transverse 0.012 - 0.015 cm/cm
0.012 - 0.015 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 25.0 MPa

@Temperature 60.0 °C
3630 psi

@Temperature 140 °F
35.0 MPa

@Temperature 23.0 °C
5080 psi

@Temperature 73.4 °F
Elongation at Break 10 %

@Temperature 23.0 °C
10 %

@Temperature 73.4 °F
70 %

@Temperature 60.0 °C
70 %

@Temperature 140 °F
>= 100 %

@Temperature 90.0 °C
>= 100 %

@Temperature 194 °F
>= 100 %

@Temperature 120 °C
>= 100 %

@Temperature 248 °F
>= 100 %

@Temperature 150 °C
>= 100 %

@Temperature 302 °F
Elongation at Yield 4.0 %
4.0 %
Tensile Modulus 0.350 GPa

@Temperature 150 °C
50.8 ksi

@Temperature 302 °F
0.450 GPa

@Temperature 120 °C
65.3 ksi

@Temperature 248 °F
0.650 GPa

@Temperature 90.0 °C
94.3 ksi

@Temperature 194 °F
1.10 GPa

@Temperature 60.0 °C
160 ksi

@Temperature 140 °F
2.70 GPa

@Temperature 23.0 °C
392 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 8.50 J/cm²
40.4 ft-lb/in²
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 90.0 °C
194 °F
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
Vicat Softening Point 160 °C

@Load 5.00 kg
320 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
V-0

@Thickness 0.750 mm
V-0

@Thickness 0.0295 in
Oxygen Index 28 %
28 %
Glow Wire Test 800 °C

@Thickness 1.00 mm
1470 °F

@Thickness 0.0394 in
GWIT
800 °C

@Thickness 2.00 mm
1470 °F

@Thickness 0.0787 in
GWIT
960 °C

@Thickness 1.00 mm
1760 °F

@Thickness 0.0394 in
GWFI/GWT
960 °C

@Thickness 2.00 mm
1760 °F

@Thickness 0.0787 in
GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 325 V
325 V
A solution
Processing Properties Metric English Comments
Melt Temperature 235 - 250 °C
455 - 482 °F
Mold Temperature 60.0 - 70.0 °C
140 - 158 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa