LATI Latamid 66 H2 G/25-V0CT1 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Glass Fiber Filled, Flame Retardant
Manufacturer LATI
Trade Name Latamid
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 66 H2 G/25-V0CT1 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.58 g/cc
0.0571 lb/in³
Linear Mold Shrinkage, Flow 0.0035 - 0.0060 cm/cm
0.0035 - 0.0060 in/in
Linear Mold Shrinkage, Transverse 0.0070 - 0.010 cm/cm
0.0070 - 0.010 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa

@Temperature 150 °C
 7250 psi

@Temperature 302 °F
60.0 MPa

@Temperature 120 °C
 8700 psi

@Temperature 248 °F
75.0 MPa

@Temperature 90.0 °C
 10900 psi

@Temperature 194 °F
95.0 MPa

@Temperature 60.0 °C
 13800 psi

@Temperature 140 °F
135 MPa

@Temperature 23.0 °C
 19600 psi

@Temperature 73.4 °F
Elongation at Break 2.1 %

@Temperature 23.0 °C
 2.1 %

@Temperature 73.4 °F
2.4 %

@Temperature 60.0 °C
 2.4 %

@Temperature 140 °F
3.8 %

@Temperature 90.0 °C
 3.8 %

@Temperature 194 °F
3.9 %

@Temperature 120 °C
 3.9 %

@Temperature 248 °F
4.2 %

@Temperature 150 °C
 4.2 %

@Temperature 302 °F
Elongation at Yield 3.5 %

@Temperature 120 °C
 3.5 %

@Temperature 248 °F
3.7 %

@Temperature 150 °C
 3.7 %

@Temperature 302 °F
Tensile Modulus 0.220 GPa

@Temperature 150 °C
 31.9 ksi

@Temperature 302 °F
3.20 GPa

@Temperature 120 °C
 464 ksi

@Temperature 248 °F
4.80 GPa

@Temperature 90.0 °C
 696 ksi

@Temperature 194 °F
7.20 GPa

@Temperature 60.0 °C
 1040 ksi

@Temperature 140 °F
9.20 GPa

@Temperature 23.0 °C
 1330 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 3.50 J/cm²
16.7 ft-lb/in²
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 115 °C
239 °F
Deflection Temperature at 0.46 MPa (66 psi) 255 °C
491 °F
Deflection Temperature at 1.8 MPa (264 psi) 240 °C
464 °F
Vicat Softening Point 245 °C

@Load 5.00 kg
 473 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
Oxygen Index 35 %
35 %
Glow Wire Test 900 °C

@Thickness 1.00 mm
 1650 °F

@Thickness 0.0394 in
 GWIT
900 °C

@Thickness 2.00 mm
 1650 °F

@Thickness 0.0787 in
 GWIT
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 400 V
400 V
A solution
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa