LATI Latamid 66 H2 G/30 PA 66, 30% Glass Fiber Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | LATI |
| Trade Name | Latamid |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latamid 66 H2 G/30 PA 66, 30% Glass Fiber Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0035 - 0.0065 cm/cm | 0.0035 - 0.0065 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0075 - 0.0105 cm/cm | 0.0075 - 0.0105 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa @Temperature 150 °C |
12300 psi @Temperature 302 °F |
|
| 100 MPa @Temperature 120 °C |
14500 psi @Temperature 248 °F |
||
| 110 MPa @Temperature 90.0 °C |
16000 psi @Temperature 194 °F |
||
| 135 MPa @Temperature 60.0 °C |
19600 psi @Temperature 140 °F |
||
| 175 MPa @Temperature 23.0 °C |
25400 psi @Temperature 73.4 °F |
||
| Elongation at Break | 3.2 % @Temperature 23.0 °C |
3.2 % @Temperature 73.4 °F |
|
| 4.0 % @Temperature 60.0 °C |
4.0 % @Temperature 140 °F |
||
| 5.5 % @Temperature 90.0 °C |
5.5 % @Temperature 194 °F |
||
| 6.0 % @Temperature 120 °C |
6.0 % @Temperature 248 °F |
||
| 6.5 % @Temperature 150 °C |
6.5 % @Temperature 302 °F |
||
| Tensile Modulus | 4.40 GPa @Temperature 150 °C |
638 ksi @Temperature 302 °F |
|
| 5.50 GPa @Temperature 120 °C |
798 ksi @Temperature 248 °F |
||
| 7.40 GPa @Temperature 90.0 °C |
1070 ksi @Temperature 194 °F |
||
| 8.50 GPa @Temperature 60.0 °C |
1230 ksi @Temperature 140 °F |
||
| 9.40 GPa @Temperature 23.0 °C |
1360 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 8.50 J/cm² | 40.4 ft-lb/in² | |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 130 °C | 266 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | |
| Vicat Softening Point | 255 °C @Load 5.00 kg |
491 °F @Load 11.0 lb |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 275 - 300 °C | 527 - 572 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 90.0 - 100 °C @Time 10800 sec |
194 - 212 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- Nilit FRIANYL B63 W-GV30 Nylon 6 for injection molding, 30% glass fiber reinforced
- MetalTek C11600 Silver Copper High Conductivity
- Kennametal Stellite Nistelle 305 Nickel Superalloy
- Borealis Borclean™ HB300BF Polypropylene Homopolymer for Capacitor Film
- A. Schulman POLYBATCH™ ASC-331 Inorganic Antislip Masterbatch Based in Polyethylene
- Teknor Apex Sinvicomp SIH 5009 Polyvinyl Chloride, Flexible
- ExxonMobil LDPE LD 159AC Low Density Polyethylene Resin
- Braskem TS7006 LDPE Blown Film Extrusion Polyethylene
- BASF Formamide
- Arkema Group KYNAR FLEX® 2950-05 Polyvinylidene Fluoride Copolymer - Extrusion & Molding
Copyright © lookpolymers.com All Rights Reserved