LATI Latamid 66 H2 G/35-V0KB1 PA 66, 35% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled , Nylon 66, Glass Fiber Filled, Flame Retardant
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 66 H2 G/35-V0KB1 PA 66, 35% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, with red phosphorous. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
Linear Mold Shrinkage, Flow 0.0030 - 0.0060 cm/cm
0.0030 - 0.0060 in/in
Linear Mold Shrinkage, Transverse 0.0075 - 0.010 cm/cm
0.0075 - 0.010 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.0 MPa

@Temperature 150 °C
 10900 psi

@Temperature 302 °F
85.0 MPa

@Temperature 120 °C
 12300 psi

@Temperature 248 °F
105 MPa

@Temperature 90.0 °C
 15200 psi

@Temperature 194 °F
140 MPa

@Temperature 60.0 °C
 20300 psi

@Temperature 140 °F
185 MPa

@Temperature 23.0 °C
 26800 psi

@Temperature 73.4 °F
Elongation at Break 2.5 %

@Temperature 23.0 °C
 2.5 %

@Temperature 73.4 °F
3.1 %

@Temperature 60.0 °C
 3.1 %

@Temperature 140 °F
4.0 %

@Temperature 90.0 °C
 4.0 %

@Temperature 194 °F
4.5 %

@Temperature 120 °C
 4.5 %

@Temperature 248 °F
4.7 %

@Temperature 150 °C
 4.7 %

@Temperature 302 °F
Tensile Modulus 4.40 GPa

@Temperature 150 °C
 638 ksi

@Temperature 302 °F
5.30 GPa

@Temperature 120 °C
 769 ksi

@Temperature 248 °F
6.30 GPa

@Temperature 90.0 °C
 914 ksi

@Temperature 194 °F
9.60 GPa

@Temperature 60.0 °C
 1390 ksi

@Temperature 140 °F
11.0 GPa

@Temperature 23.0 °C
 1600 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 7.00 J/cm²
33.3 ft-lb/in²
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 125 °C
257 °F
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Deflection Temperature at 1.8 MPa (264 psi) 255 °C
491 °F
Vicat Softening Point 255 °C

@Load 5.00 kg
 491 °F

@Load 11.0 lb
Flammability, UL94 HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Oxygen Index 27 %
27 %
Glow Wire Test 960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
A solution
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa