- LATI Latamid 66 H2 G/50 PA 66, 50% Glass Fiber Reinforced, Heat Stabilized
LATI Latamid 66 H2 G/50 PA 66, 50% Glass Fiber Reinforced, Heat Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled |
| Manufacturer | LATI |
| Trade Name | Latamid |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latamid 66 H2 G/50 PA 66, 50% Glass Fiber Reinforced, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0065 - 0.0095 cm/cm | 0.0065 - 0.0095 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa @Temperature 150 °C |
14500 psi @Temperature 302 °F |
|
| 120 MPa @Temperature 120 °C |
17400 psi @Temperature 248 °F |
||
| 140 MPa @Temperature 90.0 °C |
20300 psi @Temperature 194 °F |
||
| 170 MPa @Temperature 60.0 °C |
24700 psi @Temperature 140 °F |
||
| 215 MPa @Temperature 23.0 °C |
31200 psi @Temperature 73.4 °F |
||
| Elongation at Break | 3.0 % @Temperature 23.0 °C |
3.0 % @Temperature 73.4 °F |
|
| 4.2 % @Temperature 60.0 °C |
4.2 % @Temperature 140 °F |
||
| 5.0 % @Temperature 90.0 °C |
5.0 % @Temperature 194 °F |
||
| 6.0 % @Temperature 120 °C |
6.0 % @Temperature 248 °F |
||
| 6.5 % @Temperature 150 °C |
6.5 % @Temperature 302 °F |
||
| Tensile Modulus | 6.00 GPa @Temperature 150 °C |
870 ksi @Temperature 302 °F |
|
| 7.10 GPa @Temperature 120 °C |
1030 ksi @Temperature 248 °F |
||
| 8.00 GPa @Temperature 90.0 °C |
1160 ksi @Temperature 194 °F |
||
| 10.0 GPa @Temperature 60.0 °C |
1450 ksi @Temperature 140 °F |
||
| 17.0 GPa @Temperature 23.0 °C |
2470 ksi @Temperature 73.4 °F |
||
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 135 °C | 275 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | |
| Vicat Softening Point | 255 °C @Load 5.00 kg |
491 °F @Load 11.0 lb |
|
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
||
| HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
||
| Oxygen Index | 27 % | 27 % |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | |
| Mold Temperature | 80.0 - 110 °C | 176 - 230 °F | |
| Drying Temperature | 90.0 - 100 °C @Time 10800 sec |
194 - 212 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® E-765 Epoxy Prepreg, T300 3K PW Reinforced
- SSAB Tunnplat Aluzink 420A YP High-strength Metal-coated Steel
- STAR Thermoplastic Alloys & Rubbers StarFlex® P 7370-1000 TPE
- Techmer ES Elastoblend® PA6/6 IM1 L 33% Glass Filled
- DuPont Performance Polymers Zytel® 45HSB NC010 Nylon 66 (Unverified Data**)
- AlphaGary Evoprene™ 007 Standard SBS Thermoplastic Elastomer Compound
- 3M Safety-Walk™ 5100 Cushion Matting
- Akro-Plastic Akromid® A3 GM 10/20 S1 PA, 10% Glass Filled, 20% Mineral Filled, Cold-Impact Resistant (discont
- Samsung Cheil Industries Infino® NH-1021 PC/ABS, Unreinforced FR
Copyright © lookpolymers.com All Rights Reserved