LATI Latene® 7-V2 PP Homopolymer, Flame Retardant

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant
Manufacturer LATI
Trade Name Latene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latene® 7-V2 PP Homopolymer, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polypropylene homopolymer (PPh) based compound. UL94 V-2 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 0.940 g/cc
0.0340 lb/in³
Linear Mold Shrinkage, Flow 0.014 - 0.017 cm/cm
0.014 - 0.017 in/in
Linear Mold Shrinkage, Transverse 0.0145 - 0.0175 cm/cm
0.0145 - 0.0175 in/in
Mechanical Properties Metric English Comments
Elongation at Break >= 100 %

@Temperature 23.0 °C
>= 100 %

@Temperature 73.4 °F
>= 100 %

@Temperature 60.0 °C
>= 100 %

@Temperature 140 °F
>= 100 %

@Temperature 90.0 °C
>= 100 %

@Temperature 194 °F
Elongation at Yield 9.0 %

@Temperature 23.0 °C
9.0 %

@Temperature 73.4 °F
10 %

@Temperature 60.0 °C
10 %

@Temperature 140 °F
>= 10 %

@Temperature 90.0 °C
>= 10 %

@Temperature 194 °F
Tensile Modulus 0.300 GPa

@Temperature 90.0 °C
43.5 ksi

@Temperature 194 °F
0.600 GPa

@Temperature 60.0 °C
87.0 ksi

@Temperature 140 °F
1.40 GPa

@Temperature 23.0 °C
203 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 2.00 J/cm²

@Temperature -20.0 °C
9.52 ft-lb/in²

@Temperature -4.00 °F
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
Charpy Impact, Notched 0.0800 J/cm²

@Temperature -20.0 °C
0.381 ft-lb/in²

@Temperature -4.00 °F
0.150 J/cm²

@Temperature 23.0 °C
0.714 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 80.0 °C
176 °F
Deflection Temperature at 0.46 MPa (66 psi) 100 °C
212 °F
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
Vicat Softening Point 90.0 °C

@Load 5.00 kg
194 °F

@Load 11.0 lb
Flammability, UL94 V-2

@Thickness 3.00 mm
V-2

@Thickness 0.118 in
V-2

@Thickness 1.50 mm
V-2

@Thickness 0.0591 in
Oxygen Index 25 %
25 %
Glow Wire Test 960 °C

@Thickness 1.00 mm
1760 °F

@Thickness 0.0394 in
GWFI/GWT
960 °C

@Thickness 2.00 mm
1760 °F

@Thickness 0.0787 in
GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
A solution
Processing Properties Metric English Comments
Melt Temperature 180 - 210 °C
356 - 410 °F
Mold Temperature 20.0 - 40.0 °C
68.0 - 104 °F
Drying Temperature 80.0 - 90.0 °C

@Time 10800 sec
176 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa