LATI Latene® EP 7-V2HF PP Copolymer, Flame Retardant

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant
Manufacturer LATI
Trade Name Latene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latene® EP 7-V2HF PP Copolymer, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polypropylene copolymer (PPc) based compound. UL94 V-2 classified, halogens-based flame retardants and red phosphorous free.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 0.950 g/cc
0.0343 lb/in³
Linear Mold Shrinkage, Flow 0.0135 - 0.0165 cm/cm
0.0135 - 0.0165 in/in
Linear Mold Shrinkage, Transverse 0.0135 - 0.0165 cm/cm
0.0135 - 0.0165 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 8.00 MPa

@Temperature 90.0 °C
 1160 psi

@Temperature 194 °F
10.0 MPa

@Temperature 60.0 °C
 1450 psi

@Temperature 140 °F
12.0 MPa

@Temperature 23.0 °C
 1740 psi

@Temperature 73.4 °F
Elongation at Break >= 100 %

@Temperature 23.0 °C
 >= 100 %

@Temperature 73.4 °F
>= 100 %

@Temperature 60.0 °C
 >= 100 %

@Temperature 140 °F
>= 100 %

@Temperature 90.0 °C
 >= 100 %

@Temperature 194 °F
Elongation at Yield 5.7 %

@Temperature 23.0 °C
 5.7 %

@Temperature 73.4 °F
7.0 %

@Temperature 60.0 °C
 7.0 %

@Temperature 140 °F
7.5 %

@Temperature 90.0 °C
 7.5 %

@Temperature 194 °F
Tensile Modulus 0.350 GPa

@Temperature 90.0 °C
 50.8 ksi

@Temperature 194 °F
0.550 GPa

@Temperature 60.0 °C
 79.8 ksi

@Temperature 140 °F
1.20 GPa

@Temperature 23.0 °C
 174 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 9.00 J/cm²
42.8 ft-lb/in²
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 60.0 °C
140 °F
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C
194 °F
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
Vicat Softening Point 75.0 °C

@Load 5.00 kg
 167 °F

@Load 11.0 lb
Flammability, UL94 V-2

@Thickness 3.00 mm
 V-2

@Thickness 0.118 in
V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0591 in
V-2

@Thickness 0.750 mm
 V-2

@Thickness 0.0295 in
Oxygen Index 26 %
26 %
Glow Wire Test 750 °C

@Thickness 1.00 mm
 1380 °F

@Thickness 0.0394 in
 GWIT
775 °C

@Thickness 2.00 mm
 1430 °F

@Thickness 0.0787 in
 GWIT
850 °C

@Thickness 1.00 mm
 1560 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
A solution
Processing Properties Metric English Comments
Melt Temperature 180 - 200 °C
356 - 392 °F
Mold Temperature 20.0 - 40.0 °C
68.0 - 104 °F
Drying Temperature 70.0 - 90.0 °C

@Time 10800 sec
 158 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa
Users viewing this material also viewed the following: