LATI Later 4 G/20 PBT, 20% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer LATI
Trade Name Later
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Later 4 G/20 PBT, 20% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polybutylene Terephthalate (PBT) based compound. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
Linear Mold Shrinkage, Flow 0.0050 - 0.0075 cm/cm
0.0050 - 0.0075 in/in
Linear Mold Shrinkage, Transverse 0.012 - 0.015 cm/cm
0.012 - 0.015 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa

@Temperature 150 °C
 5800 psi

@Temperature 302 °F
45.0 MPa

@Temperature 120 °C
 6530 psi

@Temperature 248 °F
60.0 MPa

@Temperature 90.0 °C
 8700 psi

@Temperature 194 °F
75.0 MPa

@Temperature 60.0 °C
 10900 psi

@Temperature 140 °F
120 MPa

@Temperature 23.0 °C
 17400 psi

@Temperature 73.4 °F
Elongation at Break 2.7 %

@Temperature 23.0 °C
 2.7 %

@Temperature 73.4 °F
3.6 %

@Temperature 60.0 °C
 3.6 %

@Temperature 140 °F
5.5 %

@Temperature 90.0 °C
 5.5 %

@Temperature 194 °F
6.0 %

@Temperature 120 °C
 6.0 %

@Temperature 248 °F
6.2 %

@Temperature 150 °C
 6.2 %

@Temperature 302 °F
Tensile Modulus 2.60 GPa

@Temperature 150 °C
 377 ksi

@Temperature 302 °F
3.30 GPa

@Temperature 120 °C
 479 ksi

@Temperature 248 °F
4.20 GPa

@Temperature 90.0 °C
 609 ksi

@Temperature 194 °F
5.70 GPa

@Temperature 60.0 °C
 827 ksi

@Temperature 140 °F
8.50 GPa

@Temperature 23.0 °C
 1230 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 5.00 J/cm²
23.8 ft-lb/in²
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 130 °C
266 °F
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
Vicat Softening Point 205 °C

@Load 5.00 kg
 401 °F

@Load 11.0 lb
Flammability, UL94 HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
Oxygen Index 23 %
23 %
Processing Properties Metric English Comments
Melt Temperature 240 - 250 °C
464 - 482 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 110 - 130 °C

@Time 10800 sec
 230 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa