POLYMER SEARCH

LATI Latiblend 5262 PP Homopolymer/PA6

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced , Polypropylene (PP)
Manufacturer	LATI
Trade Name	Latiblend
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latiblend 5262 PP Homopolymer/PA6.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Blend based on Polypropylene homopolymer (PPh) / Polyamide 6 (PA6). Unfilled. High impact resistance. Very good elongation.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	0.970 g/cc	0.0350 lb/inÂ³
Linear Mold Shrinkage, Flow	0.013 - 0.017 cm/cm	0.013 - 0.017 in/in
Linear Mold Shrinkage, Transverse	0.014 - 0.018 cm/cm	0.014 - 0.018 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	20.0 MPa	2900 psi
Elongation at Break	150 % @Temperature 23.0 Â°C	150 % @Temperature 73.4 Â°F
Elongation at Yield	6.0 % @Temperature 23.0 Â°C	6.0 % @Temperature 73.4 Â°F
Tensile Modulus	0.750 GPa	109 ksi
Charpy Impact Unnotched	NB	NB
Charpy Impact, Notched	3.00 J/cmÂ²	14.3 ft-lb/inÂ²

Thermal Properties	Metric	English
Maximum Service Temperature, Air	70.0 Â°C	158 Â°F
Deflection Temperature at 0.46 MPa (66 psi)	80.0 Â°C	176 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	45.0 Â°C	113 Â°F
Vicat Softening Point	70.0 Â°C @Load 5.00 kg	158 Â°F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	220 - 240 Â°C	428 - 464 Â°F
Mold Temperature	70.0 - 80.0 Â°C	158 - 176 Â°F
Drying Temperature	80.0 - 90.0 Â°C @Time 10800 sec	176 - 194 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa