LATI Laticonther 57 CPG/550 PPA, Glass Fiber Reinforced

Category	Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 50% Glass Fiber Reinforced
Manufacturer	LATI
Trade Name	Laticonther
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Laticonther 57 CPG/550 PPA, Glass Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

High thermal conductivity product based on Semi-aromatic polyamide (PPA). Special filler. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.99 g/cc	0.0719 lb/in³
Linear Mold Shrinkage, Flow	0.0030 - 0.0045 cm/cm	0.0030 - 0.0045 in/in
Linear Mold Shrinkage, Transverse	0.0050 - 0.0065 cm/cm	0.0050 - 0.0065 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	70.0 MPa	10200 psi
Elongation at Break	0.60 %	0.60 %
Tensile Modulus	11.0 GPa	1600 ksi
Charpy Impact Unnotched	1.00 J/cm²	4.76 ft-lb/in²
Charpy Impact, Notched	0.200 J/cm²	0.952 ft-lb/in²

Thermal Properties	Metric	English	Comments
Thermal Conductivity	1.20 W/m-K	8.33 BTU-in/hr-ft²-°F	Longitudinal
Deflection Temperature at 0.46 MPa (66 psi)	120 °C	248 °F
Deflection Temperature at 1.8 MPa (264 psi)	90.0 °C	194 °F
Vicat Softening Point	100 °C @Load 5.00 kg	212 °F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Surface Resistance	1.00e+12 ohm	1.00e+12 ohm

Processing Properties	Metric	English
Melt Temperature	310 - 330 °C	590 - 626 °F
Mold Temperature	140 - 160 °C	284 - 320 °F
Drying Temperature	120 - 130 °C @Time 10800 sec	248 - 266 °F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa

Users viewing this material also viewed the following: