LATI Laticonther 80 CPG/700 PPS, Glass Fiber Reinforced

Category	Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer	LATI
Trade Name	Laticonther
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Laticonther 80 CPG/700 PPS, Glass Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

High thermal conductivity product based on Polyphenylene Sulfide (PPS). Special filler. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	2.55 g/cc	0.0921 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0020 - 0.0035 cm/cm	0.0020 - 0.0035 in/in
Linear Mold Shrinkage, Transverse	0.0025 - 0.0040 cm/cm	0.0025 - 0.0040 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	60.0 MPa	8700 psi
Elongation at Break	0.50 %	0.50 %
Tensile Modulus	14.0 GPa	2030 ksi
Charpy Impact Unnotched	1.00 J/cmÂ²	4.76 ft-lb/inÂ²
Charpy Impact, Notched	0.400 J/cmÂ²	1.90 ft-lb/inÂ²

Thermal Properties	Metric	English	Comments
Thermal Conductivity	1.40 W/m-K	9.72 BTU-in/hr-ftÂ²-Â°F	Longitudinal
Maximum Service Temperature, Air	220 Â°C	428 Â°F
Deflection Temperature at 0.46 MPa (66 psi)	280 Â°C	536 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	245 Â°C	473 Â°F
Vicat Softening Point	250 Â°C @Load 5.00 kg	482 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	225 V	225 V	A solution

Processing Properties	Metric	English
Melt Temperature	290 - 320 Â°C	554 - 608 Â°F
Mold Temperature	130 - 140 Â°C	266 - 284 Â°F
Drying Temperature	130 - 150 Â°C @Time 10800 sec	266 - 302 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa

Users viewing this material also viewed the following: