LATI Laticonther 80 GCE/650 PPS, Glass/Mineral Reinforced

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled
Manufacturer LATI
Trade Name Laticonther
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Laticonther 80 GCE/650 PPS, Glass/Mineral Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High thermal conductivity product based on Polyphenylene Sulfide (PPS). Glass fibers / Mineral filler.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.91 g/cc
0.0690 lb/in³
Linear Mold Shrinkage, Flow 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
Linear Mold Shrinkage, Transverse 0.0015 - 0.0030 cm/cm
0.0015 - 0.0030 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 60.0 MPa

@Temperature 150 °C
 8700 psi

@Temperature 302 °F
75.0 MPa

@Temperature 120 °C
 10900 psi

@Temperature 248 °F
115 MPa

@Temperature 90.0 °C
 16700 psi

@Temperature 194 °F
130 MPa

@Temperature 60.0 °C
 18900 psi

@Temperature 140 °F
145 MPa

@Temperature 23.0 °C
 21000 psi

@Temperature 73.4 °F
Elongation at Break 0.80 %

@Temperature 23.0 °C
 0.80 %

@Temperature 73.4 °F
1.1 %

@Temperature 60.0 °C
 1.1 %

@Temperature 140 °F
1.2 %

@Temperature 90.0 °C
 1.2 %

@Temperature 194 °F
2.0 %

@Temperature 120 °C
 2.0 %

@Temperature 248 °F
2.5 %

@Temperature 150 °C
 2.5 %

@Temperature 302 °F
Tensile Modulus 8.00 GPa

@Temperature 150 °C
 1160 ksi

@Temperature 302 °F
13.0 GPa

@Temperature 120 °C
 1890 ksi

@Temperature 248 °F
18.1 GPa

@Temperature 90.0 °C
 2630 ksi

@Temperature 194 °F
20.0 GPa

@Temperature 60.0 °C
 2900 ksi

@Temperature 140 °F
23.0 GPa

@Temperature 23.0 °C
 3340 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 1.50 J/cm²
7.14 ft-lb/in²
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Thermal Properties Metric English Comments
Thermal Conductivity 0.900 W/m-K
6.25 BTU-in/hr-ft²-°F
Longitudinal
Maximum Service Temperature, Air 225 °C
437 °F
Deflection Temperature at 0.46 MPa (66 psi) 285 °C
545 °F
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
Vicat Softening Point 260 °C

@Load 5.00 kg
 500 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 290 - 320 °C
554 - 608 °F
Mold Temperature 130 - 140 °C
266 - 284 °F
Drying Temperature 130 - 150 °C

@Time 10800 sec
 266 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa