LATI Latigloss 66 H2 K/30 PA 66, 30% Carbon Fiber Reinforced, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Carbon Fiber Filled
Manufacturer LATI
Trade Name Latigloss
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latigloss 66 H2 K/30 PA 66, 30% Carbon Fiber Reinforced, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product with high mechanical properties and exceptional surface finish based on Polyamide 66 (PA66). Heat stabilized. Carbon fiber. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
Linear Mold Shrinkage, Flow 0.0015 - 0.0035 cm/cm
0.0015 - 0.0035 in/in
Linear Mold Shrinkage, Transverse 0.0055 - 0.0085 cm/cm
0.0055 - 0.0085 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.0 MPa

@Temperature 150 °C
 9430 psi

@Temperature 302 °F
80.0 MPa

@Temperature 120 °C
 11600 psi

@Temperature 248 °F
110 MPa

@Temperature 90.0 °C
 16000 psi

@Temperature 194 °F
155 MPa

@Temperature 60.0 °C
 22500 psi

@Temperature 140 °F
230 MPa

@Temperature 23.0 °C
 33400 psi

@Temperature 73.4 °F
Elongation at Break 1.7 %

@Temperature 23.0 °C
 1.7 %

@Temperature 73.4 °F
2.6 %

@Temperature 60.0 °C
 2.6 %

@Temperature 140 °F
4.2 %

@Temperature 90.0 °C
 4.2 %

@Temperature 194 °F
4.6 %

@Temperature 120 °C
 4.6 %

@Temperature 248 °F
5.0 %

@Temperature 150 °C
 5.0 %

@Temperature 302 °F
Tensile Modulus 4.90 GPa

@Temperature 150 °C
 711 ksi

@Temperature 302 °F
6.10 GPa

@Temperature 120 °C
 885 ksi

@Temperature 248 °F
10.0 GPa

@Temperature 90.0 °C
 1450 ksi

@Temperature 194 °F
16.0 GPa

@Temperature 60.0 °C
 2320 ksi

@Temperature 140 °F
21.0 GPa

@Temperature 23.0 °C
 3050 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 3.50 J/cm²
16.7 ft-lb/in²
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 130 °C
266 °F
Deflection Temperature at 0.46 MPa (66 psi) 255 °C
491 °F
Deflection Temperature at 1.8 MPa (264 psi) 240 °C
464 °F
Vicat Softening Point 245 °C

@Load 5.00 kg
 473 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 280 - 320 °C
536 - 608 °F
Mold Temperature 90.0 - 120 °C
194 - 248 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa