LATI Latigray 80-03 CWG/850 PPS, Glass/Metallic Reinforced

Category	Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer	LATI
Trade Name	Latigray
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latigray 80-03 CWG/850 PPS, Glass/Metallic Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Radiopaque compound based on Polyphenylene Sulfide (PPS). Metallic filler. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English	Comments
Density	5.38 g/cc	0.194 lb/inÂ³
Thickness	520 microns	20.5 mil	80
	680 microns	26.8 mil	120
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm	0.0040 - 0.0060 in/in
Linear Mold Shrinkage, Transverse	0.0060 - 0.0090 cm/cm	0.0060 - 0.0090 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	85.0 MPa	12300 psi
Elongation at Break	1.1 %	1.1 %
Tensile Modulus	13.9 GPa	2020 ksi
Charpy Impact Unnotched	1.50 J/cmÂ²	7.14 ft-lb/inÂ²
Charpy Impact, Notched	0.500 J/cmÂ²	2.38 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	275 Â°C	527 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	250 Â°C	482 Â°F
Vicat Softening Point	255 Â°C @Load 5.00 kg	491 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Surface Resistance	1.00e+9 ohm	1.00e+9 ohm

Processing Properties	Metric	English
Melt Temperature	290 - 310 Â°C	554 - 590 Â°F
Mold Temperature	130 - 140 Â°C	266 - 284 Â°F
Drying Temperature	130 - 140 Â°C @Time 10800 sec	266 - 284 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa