LATI Latilub 57-10T Y/15 PPA, Aramid Reinforced

Category	Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), Aramid Fiber Filled
Manufacturer	LATI
Trade Name	Latilub
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latilub 57-10T Y/15 PPA, Aramid Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Self-lubricating product based on Semi-aromatic polyamide (PPA). PTFE. Aramid fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.28 g/cc	0.0462 lb/inÂ³
Linear Mold Shrinkage, Flow	0.011 - 0.014 cm/cm	0.011 - 0.014 in/in
Linear Mold Shrinkage, Transverse	0.012 - 0.015 cm/cm	0.012 - 0.015 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	60.0 MPa	8700 psi
Elongation at Break	2.0 %	2.0 %
Tensile Modulus	3.50 GPa	508 ksi
Charpy Impact Unnotched	1.00 J/cmÂ²	4.76 ft-lb/inÂ²
Charpy Impact, Notched	0.100 J/cmÂ²	0.476 ft-lb/inÂ²
Coefficient of Friction, Dynamic	0.24	0.24
Coefficient of Friction, Static	0.27	0.27
K (wear) Factor	5.50 x 10^-8 mmÂ³/N-M	2.73 x 10^-10 inÂ³-min/ft-lb-hr

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	240 Â°C	464 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	135 Â°C	275 Â°F
Vicat Softening Point	215 Â°C @Load 5.00 kg	419 Â°F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	310 - 330 Â°C	590 - 626 Â°F
Mold Temperature	130 - 160 Â°C	266 - 320 Â°F
Drying Temperature	120 - 130 Â°C @Time 10800 sec	248 - 266 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa