LATI Latilub 66-01M G/30 PA66, 30% Glass Fiber Reinforced, Molybdenum disulphide Filled

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber/MoS2 Filled
Manufacturer LATI
Trade Name Latilub
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 66-01M G/30 PA66, 30% Glass Fiber Reinforced, Molybdenum disulphide Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polyamide 66 (PA66). Molybdenum disulphide. Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.38 g/cc
0.0499 lb/in³
Linear Mold Shrinkage, Flow 0.0035 - 0.0065 cm/cm
0.0035 - 0.0065 in/in
Linear Mold Shrinkage, Transverse 0.0075 - 0.0105 cm/cm
0.0075 - 0.0105 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 165 MPa
23900 psi
Elongation at Break 3.1 %
3.1 %
Tensile Modulus 9.40 GPa
1360 ksi
Charpy Impact Unnotched 6.50 J/cm²
30.9 ft-lb/in²
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
Coefficient of Friction, Dynamic 0.36
0.36
Coefficient of Friction, Static 0.42
0.42
K (wear) Factor 30.0 x 10-8 mm³/N-M
14.9 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Deflection Temperature at 1.8 MPa (264 psi) 255 °C
491 °F
Vicat Softening Point 255 °C

@Load 5.00 kg
491 °F

@Load 11.0 lb
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
Processing Properties Metric English Comments
Melt Temperature 275 - 300 °C
527 - 572 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa