LATI Latilub 66 Y/20 PA66, Aramid Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Aramid Fiber Filled
Manufacturer LATI
Trade Name Latilub
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 66 Y/20 PA66, Aramid Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polyamide 66 (PA66). Aramid fibersAvailability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
Linear Mold Shrinkage, Flow 0.0095 - 0.0125 cm/cm
0.0095 - 0.0125 in/in
Linear Mold Shrinkage, Transverse 0.0105 - 0.0135 cm/cm
0.0105 - 0.0135 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa
11600 psi
Elongation at Break 3.5 %
3.5 %
Tensile Modulus 3.80 GPa
551 ksi
Charpy Impact Unnotched 2.00 J/cm²
9.52 ft-lb/in²
Charpy Impact, Notched 0.200 J/cm²
0.952 ft-lb/in²
Coefficient of Friction, Dynamic 0.22
0.22
Coefficient of Friction, Static 0.26
0.26
K (wear) Factor 12.0 x 10-8 mm³/N-M
5.96 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 240 °C
464 °F
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
Vicat Softening Point 245 °C

@Load 5.00 kg
473 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 270 - 300 °C
518 - 572 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa