LATI Latilub 80-10T Y/15 PPS, 15% Aramid Fiber Reinforced, PTFE Filled

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Aramid Fiber Filled
Manufacturer LATI
Trade Name Latilub
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 80-10T Y/15 PPS, 15% Aramid Fiber Reinforced, PTFE Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polyphenylene Sulfide (PPS). PTFE. Aramid fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
Linear Mold Shrinkage, Flow 0.0045 - 0.0075 cm/cm
0.0045 - 0.0075 in/in
Linear Mold Shrinkage, Transverse 0.0050 - 0.0080 cm/cm
0.0050 - 0.0080 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa
6530 psi
Elongation at Break 1.2 %
1.2 %
Tensile Modulus 3.80 GPa
551 ksi
Charpy Impact Unnotched 0.500 J/cm²
2.38 ft-lb/in²
Charpy Impact, Notched 0.150 J/cm²
0.714 ft-lb/in²
Coefficient of Friction, Dynamic 0.15
0.15
Coefficient of Friction, Static 0.19
0.19
K (wear) Factor 4.30 x 10-8 mm³/N-M
2.13 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
Deflection Temperature at 1.8 MPa (264 psi) 110 °C
230 °F
Vicat Softening Point 245 °C

@Load 5.00 kg
473 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 0.750 mm
V-0

@Thickness 0.0295 in
Processing Properties Metric English Comments
Melt Temperature 290 - 310 °C
554 - 590 °F
Mold Temperature 130 - 150 °C
266 - 302 °F
Drying Temperature 130 - 150 °C

@Time 10800 sec
266 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa