LATI Latilub 80-15T G/30 PPS, 30% Glass Fiber Reinforced, PTFE Filled

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), PTFE/Glass-Fiber Filled
Manufacturer LATI
Trade Name Latilub
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 80-15T G/30 PPS, 30% Glass Fiber Reinforced, PTFE Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polyphenylene Sulfide (PPS). PTFE. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.62 g/cc
0.0585 lb/in³
Linear Mold Shrinkage, Flow 0.0025 - 0.0040 cm/cm
0.0025 - 0.0040 in/in
Linear Mold Shrinkage, Transverse 0.0060 - 0.0075 cm/cm
0.0060 - 0.0075 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 120 MPa
17400 psi
Elongation at Break 1.4 %
1.4 %
Tensile Modulus 13.5 GPa
1960 ksi
Charpy Impact Unnotched 3.50 J/cm²
16.7 ft-lb/in²
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
Coefficient of Friction, Dynamic 0.17
0.17
Coefficient of Friction, Static 0.21
0.21
K (wear) Factor 8.70 x 10-8 mm³/N-M
4.32 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 275 °C
527 °F
Deflection Temperature at 1.8 MPa (264 psi) 265 °C
509 °F
Vicat Softening Point 255 °C

@Load 5.00 kg
491 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 290 - 310 °C
554 - 590 °F
Mold Temperature 130 - 150 °C
266 - 302 °F
Drying Temperature 130 - 150 °C

@Time 10800 sec
266 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa