LATI Latilub 80-15T K/30 PPS, 30% Carbon Fiber Reinforced, PTFE Filled

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with Carbon Fiber + PTFE Filler
Manufacturer LATI
Trade Name Latilub
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 80-15T K/30 PPS, 30% Carbon Fiber Reinforced, PTFE Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polyphenylene Sulfide (PPS). PTFE. Carbon fiber. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.50 g/cc
0.0542 lb/in³
Linear Mold Shrinkage, Flow 0.0015 - 0.0035 cm/cm
0.0015 - 0.0035 in/in
Linear Mold Shrinkage, Transverse 0.0025 - 0.0045 cm/cm
0.0025 - 0.0045 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 170 MPa
24700 psi
Elongation at Break 0.50 %
0.50 %
Tensile Modulus 24.0 GPa
3480 ksi
Charpy Impact Unnotched 2.00 J/cm²
9.52 ft-lb/in²
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
Coefficient of Friction, Dynamic 0.14
0.14
Coefficient of Friction, Static 0.18
0.18
K (wear) Factor 8.80 x 10-8 mm³/N-M
4.37 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 280 °C
536 °F
Deflection Temperature at 1.8 MPa (264 psi) 270 °C
518 °F
Vicat Softening Point 255 °C

@Load 5.00 kg
491 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 290 - 310 °C
554 - 590 °F
Mold Temperature 130 - 150 °C
266 - 302 °F
Drying Temperature 130 - 150 °C

@Time 10800 sec
266 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa