LATI Latilub 88/10-15T G/30 PEEK, 30% Glass Fiber Reinforced, PTFE Filled

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled
Manufacturer LATI
Trade Name Latilub
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 88/10-15T G/30 PEEK, 30% Glass Fiber Reinforced, PTFE Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polyetheretherketone (PEEK). PTFE. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.62 g/cc
0.0585 lb/in³
Linear Mold Shrinkage, Flow 0.0030 - 0.0055 cm/cm
0.0030 - 0.0055 in/in
Linear Mold Shrinkage, Transverse 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 110 MPa
16000 psi
Elongation at Break 2.0 %
2.0 %
Tensile Modulus 12.4 GPa
1800 ksi
Charpy Impact Unnotched 3.80 J/cm²
18.1 ft-lb/in²
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
Coefficient of Friction, Dynamic 0.28
0.28
Coefficient of Friction, Static 0.35
0.35
K (wear) Factor 6.80 x 10-8 mm³/N-M
3.38 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 295 °C
563 °F
Deflection Temperature at 1.8 MPa (264 psi) 255 °C
491 °F
Vicat Softening Point 350 °C

@Load 5.00 kg
662 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 370 - 400 °C
698 - 752 °F
Mold Temperature 170 - 200 °C
338 - 392 °F
Drying Temperature 120 - 150 °C

@Time 10800 sec
248 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa