LATI Latilub 88/50-20GRT K/10 PEEK, 10% Carbon Fiber Reinforced, Graphite/PTFE Filled

Category	Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Carbon Fiber Filled
Manufacturer	LATI
Trade Name	Latilub
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latilub 88/50-20GRT K/10 PEEK, 10% Carbon Fiber Reinforced, Graphite/PTFE Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Self-lubricating product based on Polyetheretherketone (PEEK). Graphite / PTFE. Carbon fiber. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.45 g/cc	0.0524 lb/in³
Linear Mold Shrinkage, Flow	0.0025 - 0.0040 cm/cm	0.0025 - 0.0040 in/in
Linear Mold Shrinkage, Transverse	0.0060 - 0.0090 cm/cm	0.0060 - 0.0090 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	145 MPa	21000 psi
Elongation at Break	2.3 %	2.3 %
Tensile Modulus	12.5 GPa	1810 ksi
Charpy Impact Unnotched	3.60 J/cm²	17.1 ft-lb/in²
Charpy Impact, Notched	0.500 J/cm²	2.38 ft-lb/in²
Coefficient of Friction, Dynamic	0.20	0.20
Coefficient of Friction, Static	0.26	0.26
K (wear) Factor	6.30 x 10^-8 mm³/N-M	3.13 x 10^-10 in³-min/ft-lb-hr

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	350 °C	662 °F
Deflection Temperature at 1.8 MPa (264 psi)	295 °C	563 °F
Vicat Softening Point	350 °C @Load 5.00 kg	662 °F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	370 - 400 °C	698 - 752 °F
Mold Temperature	170 - 200 °C	338 - 392 °F
Drying Temperature	120 - 150 °C @Time 10800 sec	248 - 302 °F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa