LATI Latilub 88/50-30GRT PEEK, Graphite/PTFE Filled

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, PTFE-Filled
Manufacturer LATI
Trade Name Latilub
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 88/50-30GRT PEEK, Graphite/PTFE Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polyetheretherketone (PEEK). Graphite / PTFE.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.48 g/cc
0.0535 lb/in³
Linear Mold Shrinkage, Flow 0.0065 - 0.0105 cm/cm
0.0065 - 0.0105 in/in
Linear Mold Shrinkage, Transverse 0.0090 - 0.013 cm/cm
0.0090 - 0.013 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 85.0 MPa
12300 psi
Elongation at Break 2.5 %
2.5 %
Tensile Modulus 5.60 GPa
812 ksi
Charpy Impact Unnotched 3.50 J/cm²
16.7 ft-lb/in²
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
Coefficient of Friction, Dynamic 0.18
0.18
Coefficient of Friction, Static 0.26
0.26
K (wear) Factor 4.70 x 10-8 mm³/N-M
2.33 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 220 °C
428 °F
Deflection Temperature at 1.8 MPa (264 psi) 165 °C
329 °F
Vicat Softening Point 280 °C

@Load 5.00 kg
536 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 360 - 390 °C
680 - 734 °F
Mold Temperature 170 - 200 °C
338 - 392 °F
Drying Temperature 120 - 150 °C

@Time 10800 sec
248 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa