LATI Latilub 95-15T PSU, PTFE Filled

Category Polymer , Thermoplastic , Polysulfone (PSU)
Manufacturer LATI
Trade Name Latilub
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 95-15T PSU, PTFE Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polysulfone (PSU). PTFE. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
Linear Mold Shrinkage, Flow 0.0105 - 0.013 cm/cm
0.0105 - 0.013 in/in
Linear Mold Shrinkage, Transverse 0.0115 - 0.0135 cm/cm
0.0115 - 0.0135 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa
13100 psi
Elongation at Break 8.0 %
8.0 %
Elongation at Yield 5.0 %
5.0 %
Tensile Modulus 1.80 GPa
261 ksi
Charpy Impact Unnotched 7.00 J/cm²
33.3 ft-lb/in²
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
Coefficient of Friction, Dynamic 0.17
0.17
Coefficient of Friction, Static 0.20
0.20
K (wear) Factor 4.50 x 10-8 mm³/N-M
2.23 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 180 °C
356 °F
Deflection Temperature at 1.8 MPa (264 psi) 170 °C
338 °F
Vicat Softening Point 180 °C

@Load 5.00 kg
356 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 290 - 320 °C
554 - 608 °F
Mold Temperature 90.0 - 110 °C
194 - 230 °F
Drying Temperature 110 - 130 °C

@Time 10800 sec
230 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa