LATI Latimass 52/11-04 D008 PP Homopolymer

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer LATI
Trade Name Latimass
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latimass 52/11-04 D008 PP Homopolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Specific density compound based on Polypropylene homopolymer (PPh). Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 0.810 g/cc
0.0293 lb/in³
Linear Mold Shrinkage, Flow 0.011 - 0.014 cm/cm
0.011 - 0.014 in/in
Linear Mold Shrinkage, Transverse 0.0105 - 0.0135 cm/cm
0.0105 - 0.0135 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 15.0 MPa
2180 psi
Elongation at Break >= 100 %
>= 100 %
Elongation at Yield 4.0 %
4.0 %
Tensile Modulus 2.20 GPa
319 ksi
Charpy Impact Unnotched 2.00 J/cm²
9.52 ft-lb/in²
Charpy Impact, Notched 0.130 J/cm²
0.619 ft-lb/in²
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 100 °C
212 °F
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
Vicat Softening Point 100 °C

@Load 5.00 kg
212 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 190 - 220 °C
374 - 428 °F
Mold Temperature 50.0 - 70.0 °C
122 - 158 °F
Drying Temperature 80.0 - 90.0 °C

@Time 10800 sec
176 - 194 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa