LATI Latiohm 62-08 PD02 G/30 PPA, 30% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer LATI
Trade Name Latiohm
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latiohm 62-08 PD02 G/30 PPA, 30% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Dissipative product based on Polyamide 6 (PA6). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
Linear Mold Shrinkage, Flow 0.0040 - 0.0055 cm/cm
0.0040 - 0.0055 in/in
Linear Mold Shrinkage, Transverse 0.0055 - 0.0080 cm/cm
0.0055 - 0.0080 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.0 MPa
10900 psi
Elongation at Break 2.0 %
2.0 %
Tensile Modulus 8.60 GPa
1250 ksi
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 205 °C
401 °F
Deflection Temperature at 1.8 MPa (264 psi) 155 °C
311 °F
Vicat Softening Point 160 °C

@Load 5.00 kg
320 °F

@Load 11.0 lb
Electrical Properties Metric English Comments
Volume Resistivity 8.00e+10 ohm-cm
8.00e+10 ohm-cm
Surface Resistance 5.00e+10 ohm
5.00e+10 ohm
Processing Properties Metric English Comments
Melt Temperature 240 - 280 °C
464 - 536 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa